Bi2Te2.7Se0.3/Cu core/shell powders were prepared by electroless plating and hydrogen reduction,and then sintered into bulk by spark plasma sintering in order to improve the thermoelectric and mechanical properties of n-type Bi-Te thermoelectric material.
【机 构】
：
State-owned Machinery Factory in Wuhu, Wuhu 241007, China;School of Materials Science & Engineering,
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Bi2Te2.7Se0.3/Cu core/shell powders were prepared by electroless plating and hydrogen reduction,and then sintered into bulk by spark plasma sintering in order to improve the thermoelectric and mechanical properties of n-type Bi-Te thermoelectric material.After electroless plating,with the increasing of Cu content,Seebeck coefficient keeps increasing and power factor enhances significantly.The highest power factor increases by three times and reaches 23.8 W·cm-1·K-2 at room temperature in Bi2Te2.7Se0.3 with 0.22wt％ Cu sample,which means electrical transport properties of Bi2Te2.7Se0.3/Cu samples have been improved.Meanwhile,the ZT values of Bi2Tez7Se0.3/Cu samples can be enhanced at different temperature zone by adjusting the Cu content.Bi2Te2.7Se0.3 with 0.05wt％ Cu sample has the best thermoelectric properties in high temperature zone,and the ZTpeak value increases from 0.35 to 0.85 at 623 K.When the Cu content increases to 0.15wt％,the ZTpeak value moves to the low temperature (373 K) and increases from 0.24 to 0.71.At the same time,the mechanical properties increases with the increasing of Cu content.
其他文献
A novel semisolid micro fused-casting (MFC) for preparing A356 alloy strips is proposed, and the effects of process parameters of pouring temperature on the microstructure and properties of A356 alloy strips are investigated. MFC means that the semisolid
A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12％Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the coatings were analyzed by SEM and XRD,
The spontaneous magnetic transitions and corresponding magnetoelastic properties of intermetallic compounds RMn2Ge2 (R=Gd, Tb and Dy) were investigated by using the X-ray diffraction method and magnetic measurement. The results showed that the compounds e
The presents preparation and characterization of different types of lignocellulosic fillers (pine wood saw-dust/ walnut shell flour/ black rice husk powder) reinforced polypropylene composites were presented. The effect of MAPP as coupling agent (4wt％) on
Bi0.5Sb1.5Te3/Cu core/shell powders were prepared by electroless plating and hydrogen reduction, and then sintered into bulk by spark plasma sintering. After electroless plating, with increasing the Cu content, the electrical conductivity keeps enhancing
Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content (5 at％ Cr) will lead to decrease in the melting point, and improves the viscosity o
BiOI nanosheets with high sorption capacity were successfully prepared by the simple hydrothermal method followed by calcination. The features of the as-obtained BiOI nanosheets were characterized by X-ray diffraction (XRD), Fourier transform infrared spe
The as-cast pure magnesium (Mg), with a purity of 99.99％, was hot-extruded at 300℃ to prepare a Mg bar with a diameter of 8 mm. The microstructure and mechanical properties of the sample before and after extrusion were investigated. The results show that
Through finite element numerical simulation and based on laminated plate theory, the effect of dimension on the torsion properties of uniform C/SiC composites pipe was studied to provide a theoretical guidance for preparing the C/SiC pipe with different d
The effect of strains on the thermal conductivity of Si/Ge superlattices was investigated by nonequilibrium molecular dynamics(NEMD)simulation.The thermal conductivities experienced a near linear drop with increasing tensile and compressive strains.It was