我厂生产的175F汽油机弹簧支承座(见图1)材料为45~#钢,要求HRC28~34。原热处理采用正常工艺:840±10℃加热淬火、回火。处理后磁力探伤微裂纹工件占40~60%。裂纹呈放射状。
I plant 175F gasoline engine spring seat (see Figure 1) material is 45 ~ # steel, HRC28 ~ 34 required. The original heat treatment using normal technology: 840 ± 10 ℃ heating quenching and tempering. After processing the magnetic detection of micro-cracks 40-60% of the workpiece. Cracks were radial.