The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with salts cured for 3 d increased;the amount of pores larger than 100 nm increased because of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d;coarse pores lager than 1000 nm in cement pastes containing NaCl and Na2SO4 increased.
The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration The degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with For 3 d increased;the amount of pores larger than 100 nm increased due of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d; coarse pores lager than 1000 nm in Cement pastes containing NaCl and Na2SO4 increased.