论文部分内容阅读
制备了一系列添加不同含量F助剂的NiWF( x)/γ-Al2 O3催化剂，并采用X射线衍射( XRD)、N2吸附、X射线光电子能谱( XPS)、NH3-TPD和高分辨透射电子显微镜( HRTEM)等手段对其结构和物化性质进行了表征，同时在固定床反应器上考察了其加氢脱氮( HDN)和加氢脱硫( HDS)活性，反应原料为中国内蒙中低温煤焦油。结果显示，随着F含量的增加，催化剂孔容和孔径没有明显变化，但比表面积减小。催化剂在643 K下硫化6 h后，其硫化度随着F含量的增加而减少，强酸位数和总酸位数呈现先略微增加后减少的趋势。高分辨透射电子显微镜测试表明，硫化后的催化剂中含有具有典型层状结构的WS2。 F含量对NiWF( x)/γ-Al2 O3的煤焦油HDN性能有较大影响，但对其HDS活性影响很弱。“,”A series of NiWF(x)/γ-Al2O3 catalysts were prepared by adding different amounts of ammonium fluoride, and the effects of fluoride amount on the structure and physicochemical properties were investigated with X-ray diffraction, X-ray photoelectron spectroscopy, NH3-TPD and high resolution transmission electron mcroscopy( HRTEM) techniques and N2 sorption experiment. Their hydrodenitrogenation (HDN) and hydrodesulfurization (HDS) catalytic performances were evaluated in a fix-bed reactor with low and middle-temperature coal tar obtained from Inner Mongolia as feedstock. Although fluoride amount has little effect on the pore diameter and pore volume of the catalysts, increase of the fluoride amount decreases the specific surface area. In addition, the sulfidation degree of the catalyst decreases with the fluoride amount when it is sulfided at 643 K for 6 h. Also, the numbers of strong acid sites and total amount acid sites change with increasing fluoride amount. They slightly increase at first, but then obviously decrease. HRTEM shows that WS2 slabs have a typical layered structure. The catalytic activity of NiWF(x)/γ-Al2 O3 for HDN and HDS of coal tar shows a volcanic trend with the fluoride amount.