将上海重型机器厂的S271钢在HFETR上进行了辐照考验。用冲击韧性和室温拉伸性能对其中子辐照脆性作了检验,确定了它们的转变温度的升高和上平台能量(USE)的降低。结果表明:在
【机 构】
：
中国核动力研究设计院,中国核动力研究设计院 四川rrrrrrrrn,四川
论文部分内容阅读
将上海重型机器厂的S271钢在HFETR上进行了辐照考验。用冲击韧性和室温拉伸性能对其中子辐照脆性作了检验,确定了它们的转变温度的升高和上平台能量(USE)的降低。结果表明:在288℃,～3×10~(19)n/cm~2辐照后,T×T/4试样的脆性转变温度的增值仅为41～43℃;从给水管套料的辐照脆化看,则是纵向小于切向;三种试样的USE都大于160J。
S271 steel at Shanghai Heavy Machinery Factory was tested for irradiation on HFETR. The neutron irradiation brittleness was tested with impact toughness and room temperature tensile properties, and their transition temperatures and the reduction of the upper platform energy (USE) were determined. The results show that the brittle transition temperature of T × T / 4 sample increases only from 41 ℃ to 43 ℃ after irradiated with ~ 3 × 10 ~ (19) n / cm ~ 2 at 288 ℃. Irradiation embrittlement to see, it is less than the longitudinal tangential; USE three samples are greater than 160J.
其他文献
目的:探讨奥沙利铂联合希罗达方案(XELOX)和紫杉醇联合氟尿嘧啶及顺铂(PCF)方案治疗晚期胃癌的疗效和毒副反应的比较。方法:对我科2005年5月至2007年10月间采用XELOX化疗方案
随着社会的不断发展,自主学习能力的具备不仅能够锻炼学生的学习能力,培养学生的科学素养,而且,对提高学生的社会竞争能力也有着巨大的作用。但是,在应试教育思想的影响下,我
随着手机的普及及人们生活水平的提高,大学生手机依赖是近些年来学校学生管理中出现的重要问题.学生在校期间不正当使用手机会给学生的心理发展和身体健康造成诸多负面影响,
目的 分析研讨小儿留置针皮下潜行穿刺降低穿刺点渗血发生率状况.方法 选取我院2015年12月-2016年7月期间门诊儿童输液中心100例0-3岁给予四肢进行留置针穿刺的患儿,将其依据
目的 研究广基的结直肠息肉患者行内镜黏膜下剥离术治疗的临床效果.方法 临床纳入86例我院2014年6月至2015年6月期间收治的广基结直肠息肉患者作为研究对象,按床位单双号分为
目的 探析核酸检测与酶免检测在血液标本安全性检测中的应用误区.方法 选取2016年1月到2016年9月在本站检验的血液标本11829例,将每份血液样本留取于NAT与ELISA样管,对其进行
目的 分析研讨微创接骨板治疗四肢长骨干骨折的临床效果及安全性.方法 本次研究对象选取我院2015年3月至2016年3月期间接受微创接骨板技术治疗的其中的18例四肢长骨干骨折患
由国际原子能机构(IAEA)组织,我国国家核安全局及核工业总公司国际合作局(IAEA事务办公室)协助安排,利用联合国开发署对我国国家核安全局的援助项目CPR/09/006和IAEA与中国
目的 回顾性分析既往2011年-2014年,新生儿脑膜炎(new born meningitis,NBM)临床特征,尝试构建早期诊断治疗体系.方法 2011年-2014年,新生儿科共收治NBM104例,调取资料,描述
目的 分析小儿接种乙肝疫苗不良反应.方法 将2014年4月至2016年5月在某社区接受乙肝疫苗治疗的350例小儿作为研究对象,其中出现不良反应的有67例小儿.结果 小儿接种乙肝疫苗