The fractions of one metallocene-based (mPE) and one conventional (znPE) ethylene-butene copolymer eluted at from temperature rising elution fractionation were selected for DSC and time-resolved small angle X-ray scattering (SAXS) and wide angle X-ray scattering (WAXS) characterization. The DSC and WAXS results show that two crystal structures exist in both mPE and znPE: structure A with higher melting temperature and structure B with lower melting temperature. It was found that original znPE (s-znPE) contains more highly ordered structure A than original mPE (s-mPE) in spite of the higher comonomer content of znPE. Another structure C is also identified because of higher crystallinity measured by WAXS than by DSC and is attributed to the interfacial region. The SAXS data were analyzed with correlation function and two maxima were observed in s-mPE and s-znPE, in agreement with the conclusion of two crystal populations drawn from DSC and WAXS results. These two crystal populations have close long periods in s-mPE, but very different long periods in s-znPE. In contrast, freshly crystallized mPE and znPE (f-mPE and f-znPE) contain only a single crystal population with a broader distribution of long period The fractions of one metallocene-based (mPE) and one conventional (znPE) ethylene-butene copolymer eluted at from temperature rising elution fractionation were selected for DSC and time-resolved small angle X-ray scattering (SAXS) and wide angle X-ray The WAXS characterization. The DSC and WAXS results show that two crystal structures exist in both mPE and znPE: structure A with higher melting temperature and structure B with lower melting temperature. It was found that original znPE (s-znPE) contains more highly ordered structure A than original mPE (s-mPE) in spite of the higher comonomer content of znPE. Another structure C is also identified because of higher crystallinity measured by WAXS than by DSC and is attributed to the interfacial region. analyzed with correlation function and two maxima were observed in s-mPE and s-znPE, in agreement with the conclusion of two crystal structures drawn from DSC and WAXS results. These two crystal populations have close long periods in s-mPE, but very different long periods in s-znPE. In contrast, freshly crystallized mPE and znPE (f-mPE and f-znPE) contain only a single crystal population with a broader distribution of long period