点焊镀锌钢板之所以困难,是由于锌的熔点(419.5℃)与钢的熔点(1500℃左右)相差太大,锌的沸点(907℃)太低,而影响生成熔核,造成电极头沾锌、熏污,破坏镀层。为此采用加大电极
论文部分内容阅读
点焊镀锌钢板之所以困难,是由于锌的熔点(419.5℃)与钢的熔点(1500℃左右)相差太大,锌的沸点(907℃)太低,而影响生成熔核,造成电极头沾锌、熏污,破坏镀层。为此采用加大电极压力,冲破镀锌层;使电极头能与钢板紧密接触;加强对电极头的冷却,以防止电极头被锌展沽污和镀层被破坏。我厂用的镀锌钢板的厚度为0.8～1.5毫米,镀锌层厚
The reason why the spot welding of galvanized steel is difficult is that the difference between the melting point of 419.5 ℃ and the melting point of steel (about 1500 ℃) is too large. The boiling point of zinc (907 ℃) is too low, which affects the nugget, Zinc dip, smoked, damaged coating. For this purpose, the electrode pressure is increased to break through the galvanized layer; the electrode head can be in close contact with the steel plate; the cooling of the electrode tip can be strengthened to prevent the electrode tip from being tarnished and the coating being damaged. The thickness of galvanized steel used by our factory is 0.8 ~ 1.5mm, and the galvanized layer is thick
其他文献
廊坊杨是廊坊市农林科学院3代科技人员历经20余年精选出来的工业用材的优良树种,具有速生、优质、高产和抗光肩星天牛危害以及耐瘠薄、耐干旱、耐盐碱等特点。廊坊杨1号、2号
论述了高校图书馆开展社会化服务的意义。以河北交通职业技术学院图书馆为例,介绍了高校图书馆开展社会化服务的相关举措。
The significance of social service in univers
党性对于高校基层党员干部而言是非常重要的,是其立身、立业、立言以及立德的重要基础。笔者主要分析了当前高校党性教育存在的主要问题,并有针对性的提出了一些问题解决策略
It is learnt from the Secretariate of Chinese Society of Marine Geologythat the First International Conference on Asian Marine Geology will be heldin Shanghai o
干部教育培训的素质和能力关系到一个地域经济社会的全面发展。面对干部教育培训形式的日益严峻和挑战,文山州要提高各级党员领导干部的能力,就必须以现代教育理念引领干部教
焊缝接头的晶间腐蚀,是浓硝酸生产中铝制设备很快破坏的主要原因。评定铝焊缝接头的晶间腐蚀倾向的方法有数种。最广泛采用的是:在50％硝酸中的试验法(耐腐蚀准数
Intergranu
为了获得高强度的铜钎焊接头,必须从被铜钎焊的铸铁表面消除片状石墨。本文研究了消除石墨的方法对灰铸铁钢钎焊接头的金相组织和剪切强度的影响。
In order to obtain hig
(特约记者赵凤)近日,内蒙古图书馆的科研项目《通用蒙古文著者号码表》通过文化部鉴定。这是该馆断“蒙古文机读目录数据库”科研项目之后,在少数民族语言文字文献信息处理
坡口加工质量的好坏,对焊接质量的影响甚大。它直接关系到焊缝成形及根部熔透情况。对于厚板,如果坡口角度不当,还会出现裂纹。为此,开好坡口至关重要。机械加工开坡口的方
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.