【摘 要】
：
The interfacial transition zone (ITZ) between the aggregates and the bulk paste is the weakest zone of ordinary concrete, which largely determines its mechanical and transporting properties. However, a complete understanding and a quantitative modeling of
【机 构】
：
School of Materials Science and Engineering, Shijiazhuang TieDao University, Shijiazhuang 050043, Ch
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The interfacial transition zone (ITZ) between the aggregates and the bulk paste is the weakest zone of ordinary concrete, which largely determines its mechanical and transporting properties. However, a complete understanding and a quantitative modeling of ITZ are still lacking. Consequently, an integrated modeling and experimental study were conducted. First, the theoretical calculation model of the ITZ volume fraction about the rotary ellipsoidal aggregate particles was established based on the nearest surface function formula. Its calculation programs were written based on Visual Basic 6.0 language and achieved visualization and functionalization. Then, the influencing factors of ITZ volume fraction of the ellipsoidal aggregate particles and the overlapping degree between the ITZ were systematically analyzed. Finally, the calculation models of ITZ volume fraction on actual ellipsoidal aggregate were given, based on cobblestones or pebbles particles with naturally ellipsoidal shape. The results indicate that the calculation model proposed is highly reliable.
其他文献
LDHs was introduced into 70# asphalt binder by different weight ratio. Asphalt penetration test, soft point test, ductility test, viscosity test, dynamic shear rheometer (DSR) test and Fourier transform infrared (FTIR) test, were conducted to characterize
Slag glass melting is usually performed on a laboratory scale in crucibles, which are economically viable tools for the production of slag glass-ceramics. In this work, quaternary CaO-Al2O3-MgO-SiO2 (CAMS) glass-ceramics were prepared by melting the taili
The microstructural evolution of C-(A)-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt％ Na2SO4 solution for different ages was comparatively investigated, by means of 29Si NMR spectroscopy, and SEM-EDS analysis. Additionally, molecular
Ferroelectric and leakage properties are important for ferroelectric applications. Pure and Nd-doped (x=0.05-0.20) BiFeO3 thin films were fabricated by sol-gel method on FTO substrates. The phase structure, surface morphology, leakage current, ferroelectr
Amphiphilic CS-SA polymers were prepared using the SA modified by small molecule water-soluble chitosan, and CS-SA nanomicelles and FF/CS-SA nanomicelles were prepared by using CSSA polymers as the material with dialysis-ultrasound method. CS-SA polymers,
A modified Bridgman directional solidification technique was used to prepare Fe-Al-Ta eutectic in situ composites at different growth rates ranging from 6 to 80 μm/s. The directionally solidified Fe-Al-Ta eutectic composites are composed of two phases: Fe
Early hydration mechanism of cement-based materials with silica fume, nano-SiO2 and silica sol of different contents was investigated, and the detailed effect of these Si-rich mineral admixtures in three stages of early hydration (NG, I, D) using kinetics
In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the c
The preparation of hydroxyl chromium oxide by hydrogen reduction of disodium chromate and particulate hydroxyl mechanical activation features were studied. Then with self-made hydroxyl chromium as the raw material, a direct reduction and carburization pro
Based on the ABAQUS / Explicit finite element method, the forming force changing trend of deep drawing test for 6A16 aluminum alloy plate after pre-aging and storage at room temperature for one month was simulated under friction coefficient ranging from 0