【摘 要】
：
Eu3+-WO3 nanoparticles were successfully prepared by the modified method of Pechini.The prepared samples were characterized by X-ray diffraction (XRD),transmiss
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Eu3+-WO3 nanoparticles were successfully prepared by the modified method of Pechini.The prepared samples were characterized by X-ray diffraction (XRD),transmission electron microscopy (TEM),high resolution transmission electron microscopy (HRTEM),and UV-vis spectroscopy.Results showed that the Eu3+-WO3 nanoparticles,which had an average external diameter of 10-25 nm,were composed of the different shapes of puncheon and catenary after being pretreated by pH,pressure vessal,and surfactant.Moreover,structural transformation matrix contained different crystals of anorthic and orthorhombic structure.The photocatalytic activities of the nanoparticles were evaluated by photocatalytic decomposition of rhodamine B.Eu3+-WO3 nanoparticles were more efficient than WO3 and TiO2 on sunlight use ratio.Photocatalysis experiments indicated that the Eu3+-WO3 nanoparticles exhibited the highest photocatalytic activity.
其他文献
内部控制是事业单位适应市场竞争的重要手段,对其健康发展有着重要意义。本文分析了事业单位内部控制存在的问题,进而提出完善内部控制的具体措施。
Internal control is an
随着科技的进步，时代的发展，全球经济逐渐一体化，我国所面对的市场竞争也日益激烈。对于市场中的企业而言，原有的竞争规则被打破，供应链之间的竞争逐渐凸显。整个世界经济被环球物
CS研究所是一家发展迅速的高新技术企业,目前正处于成长期,保持企业的高绩效是企业发展的关键所在。然而,由于公司人力资源管理长期相对薄弱,也影响了绩效管理的有效执行。因
由于当前国际工程承包市场竞争激烈，承包商价格在压缩工程成本的基础上还需要保证工程质量，因此，需要从工程项目投标开始做好预算，最大限度地提高工程项目的经济效益，增强企业在国
采用电弧离子镀技术制备了不同成分的Cr-O-N薄膜作为NiCrAlY涂层与高温合金基材DSM11之间的扩散阻挡层.研究了不同O2和N2流量对Cr-O-N薄膜的相含量的影响及对NiCrAlY/Cr-O-N/
当前国有企业的改革正处于建立现代化企业制度的攻坚阶段,逐步建立起现代化企业制度,公司结构逐渐趋于完整,这就为内部审计提供了有利的内部条件,因此,如何搞好企业内部控制
得控则强,失控则弱,无控则乱。建设内控体系,关键在执行,本文对我国拟上市企业内控体系落地难的原因进行分析,并针对性的提出推动内控制度实施的操作建议,为拟上市企业顺利推
随着市场经济的快速发展,合同管理在经济活动中的地位也越显重要,如何把好合同关、通过内控约束合同管理,防范各类法律风险,确保企业的正当利益不受损失,已成为企业迫切需要
Experimental electron momentum density of γ-Ce was measured at an intermediate resolution (0.38 a.u.) using 20 Ci 137Cs Compton spectrometer. The experiment wa
The goal of this work was aimed to improve the power conversion efficiency of single crystalline silicon-based photovoltaic cells by using the solar spectral co