【摘 要】
：
铸造镍基合金M38经过功率密度为2.3×10~4W/cm~2、连续CO_2激光束作用0.2秒处理后,形成了0.6毫米厚树枝胞状晶的表层;大量的TIC被固溶;γ’相及M23C6相重新以更细小的颗粒析
【机 构】
：
中国科学院金属腐蚀与防护研究所,中国科学院金属腐蚀与防护研究所,中国科学院金属腐蚀与防护研究所,
论文部分内容阅读
铸造镍基合金M38经过功率密度为2.3×10~4W/cm~2、连续CO_2激光束作用0.2秒处理后,形成了0.6毫米厚树枝胞状晶的表层;大量的TIC被固溶;γ’相及M23C6相重新以更细小的颗粒析出在晶内或晶界上,晶粒的平均直径由0.2—0.3mm减少到～0.01mm;熔区晶粒内的含铬量略有增加;经900℃下的坩锅熔盐法试验,激光处理层较未激光处理层表现出良好的抗热腐蚀性能,特别是显著地减少了沿晶腐蚀.
After casting nickel-based alloy M38 with a power density of 2.3 × 10 ~ 4W / cm ~ 2 and a continuous CO_2 laser beam for 0.2 seconds, a superficial 0.6mm thick dendritic cell was formed; a large amount of TIC was dissolved; And M23C6 phase re-finer particles precipitated in the grain or grain boundary, the average grain diameter decreased from 0.2-0.3mm ~ 0.01mm; the melting zone grain chromium content slightly increased; 900 ℃ Under crucible molten salt test, the laser-treated layer showed better resistance to hot corrosion than the non-laser-treated layer, especially the intergranular corrosion was significantly reduced.
其他文献
侧柏是陇东黄土高原区的乡土树种,自然状态下常在险坡、峭壁生长,极耐干旱、瘠薄,是当地干旱山坡、强阳陡坡造林中不可多得的造林树种,也是园林绿化中的常用树种。过去,采用
家喻户晓的大明星杜明汉(王力宏饰)虽然事业发达,人生看似顺遂写意,但他内心偶尔总会感到空虚遗憾。直到有一次,杜明汉的保姆车意外撞上音乐系女学生宋晓青(刘亦菲饰),宋晓青
内螺纹的总检一般包括四个量:螺纹中径、螺纹轴线与外圆柱轴线之间轴度、螺纹轴线与其端面的垂直度和螺纹深度。它们的检测一般都是手工,其典型零件如图1。
The general in
前言电子计算机在工业中的应用越来越受到广泛重视,它对提高企业的工作效率和生产率有很大意义。我国各行各业也正在开展电子计算机的研究和应用.实践证明,凡是使用电子计算
我厂生产的3Z3.5—9.2/30型氧气压缩机气缸套(图1所示),最初采用传统的刚性结构夹具,外圆磨削后卸下夹具放置4小时后,实测圆柱度达0.17mm,严重影响了产品质量。对此,我厂进
西德DIN(国家工业标准)中有缩短钻头横刃的规定(如图1)。但是,该规定尚不充分,专家们仍注意研竟钻头刃磨方法对于孔加工精度等的影响,西德GUHRING公司最近针对钻头的刃磨方
对W18Cr4V轧后退火材,一次淬火(1285℃,4min油淬)断口上闪点缺陷,经宏观,微观断口观察;奥氏体晶粒测定;等温退火变形量、终变温度与轧后退火工艺以及使用寿命的验证试验,找出
高精度冲模大都采用滚珠导套。在导柱和导套之间配有滚珠套。每个套镶有滚珠96个。加工时需在滚珠套上钻孔,但需留120°锥度不完全穿透,然后放入滚珠,最后用镶珠杆将滚珠镶
在机械加工中常遇到偏心零件,下面介绍一种为C620车床设计的偏心卡盘座(附图)。用螺钉7和定位销6将半螺母4紧固在法兰座2上。滑动座1和法兰座2之间以半螺母4为导向键,可以自
刀具是金属切削加工的重要工具之一。它对发挥机床性能、提高生产率、保证加工质量、降低加工成本都有很大作用。特别是新型刀具的出现,常常把劳动生产率和加工质量提高到一