【摘 要】
：
In order to explore the effect of high-temperature annealing on the mechanical performances and microstructures of different oxygen SiC fibers, two types of silicon carbide (SiC) -based fibers, specified as XD-SiC fibers (low oxygen) and Nicalon-201 fiber
【机 构】
：
School of Materials Science and Engineering, Beihang University, Beijing 100086, China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In order to explore the effect of high-temperature annealing on the mechanical performances and microstructures of different oxygen SiC fibers, two types of silicon carbide (SiC) -based fibers, specified as XD-SiC fibers (low oxygen) and Nicalon-201 fibers (high oxygen), were annealed in Ar for 1 h at 800 ℃, 1 000 and 1 200 ℃, respectively. Mechanical properties of these fibers were characterized via a monofilament tensile method, with observation of the damaged monofilament by SEM. Also, the effects of annealing on the microstructure and chemical compositions of the fibers were studied. The experimental results indicated that the tensile strength decreased with the increase of annealing temperatures, after annealing-treatment at 1200℃, XD-SiC fibers remained 84％ of its original strength, while Nicalon-201 fibers remained only 58％ of its original strength. Crystallization and chemical composition of the fibers are the dominating factors for their mechanical performance at high temperatures. The microstructure changes of XD-SiC fibers are mainly composed of the growth of β-SiC, for Nicalon-201 fibers, evaporation of gases is the main change for microstructure.
其他文献
The p-type Ge doped Fe0.4Co3.6Sb12-xGex skutterudites with multi-scaled impurity dots (500 nm-2 mm) were successfully prepared by using melt-quenching (MQ) and subsequent spark plasma sintering (SPS) technique. Compared with traditional method, the new te
The CaCu3Ti4O12 (CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process (synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investiga
The dimpling defects caused by conventional hemispherical punch in doubly curved sheet metal reconfigurable die forming process were considered. The rotatable cubic punch (RCP) was developed to suppress the dimpling defects more effectively and convenient
La0.8Sr0.2MnO3 samples with rhombohedral, orthohombic and monoclinic structures were prepared by solid state reaction, sol-gel and co-precipitation methods, respectively. Lattice parameters, grain size, morphology, infrared absorption and emissivity of sa
Catalyst enhanced chemical vapor deposition of nickel film on high Tg polymers such as teflon (PTFE), polyimide(PI), and polysulfone(PS) was investigated by hot wall and cold wall CVD, in which Ni(dmg)2, Ni(acac)2, Ni(hfac)2, Ni(TMHD)2, and Ni(cp)2 are us
Nano-ZrO2 and PEEK particles were synergistically filled in unfilled PTFE to improve the wear resistance and maintain a relatively low friction coefficient, and the materials were studied using a reciprocating sliding friction and wear tester. In the fric
A post-treatment of hydrothermal process was conducted to evaluate its effects on the material characteristics and mechanical properties of plasma-sprayed pure HA and HA/20％ YSZ coatings. Surface morphology and microstructural changes, relative element co
The polymeric admixture,the sodium-carboxymethylcellulose (CMC)/poly sodium p-styrene sulfonate (PSS) / poly vinyl acetate (PVAc) was synthesized and applied in cement mortars.The polymer was tested by FTIR and SEM,and the results indicate that the ideal
The nucleation process of graphene films prepared by pulsed laser deposition has been investigated in detail. It is found that graphene nucleates at the steps on the substrate surface firstly, from aggregation of nuclei into particles. High pulsed laser e