介绍了机车用橡胶减振制品硫化成型过程中模腔压力的采集方法,综述了现阶段橡胶减振制品成型过程中关于“压力”对制品性能影响的研究成果与进展,并对未来模腔压力的应用进行了展望.
橡胶减振制品模腔压力研究进展
【摘 要】
：
介绍了机车用橡胶减振制品硫化成型过程中模腔压力的采集方法,综述了现阶段橡胶减振制品成型过程中关于“压力”对制品性能影响的研究成果与进展,并对未来模腔压力的应用进行了展望.
【机 构】
：
株洲时代新材料科技股份有限公司,湖南株洲 412007
【出 处】
：
特种橡胶制品
【发表日期】
：
2021年4期
其他文献
Lithium sulfur (Li-S) batteries are the promising power sources, but their commercialization is signifi-cantly impeded by poor energy-storage functions at high sulfur loading. Here we report that such an issue can be effectively addressed by using a musse
从氯丁橡胶的防护体系、增塑剂和补强填充剂等方面对其耐热老化性能进行了研究.结果表明,防护体系采用防老剂ZA/NBC和微晶蜡并用,增塑剂使用TOTM/TP95,补强填充体系选择无机填料和炭黑并用可有效提升氯丁橡胶的耐热老化性能.
Poly (ethylene-oxide) (PEO)-based membranes have attracted much attention recently for CO2 separation because CO2 is highly soluble into PEO and shows high selectivity over other gases such as CH4 and N2. Unfortunately, those membranes are not strong enou
Hybrid architecture design enhances the areal capacity and cycling life of low-overpotential nanoarr
Transition metal oxide (TMO) nanoarrays are promising architecture designs for self-supporting oxygen electrodes to achieve high catalytic activities in lithium-oxygen (Li- O2) batteries. However, the poor con-ductive nature of TMOs and the confined growt
研究了NBR的耐臭氧性能、物理性能、热老化性能以及耐1RM903油性能的变化.结果表明,在NBR配方中添加微晶蜡和防老剂4020可提高胶料的耐臭氧性能,且随着用量的增加,耐臭氧性能逐渐增大.当微晶蜡与4020用量分别为3份与2份时,硫化胶试样满足在拉伸20％、温度40℃、臭氧浓度为50×10-8、时间为72h下无龟裂要求.与不添加微晶蜡与4020的原配方相比,两者在硫化特性、物理性能、热老化性能和耐IRM903油性能方面无明显差别.
研究了高苯乙烯橡胶HS-630在天然橡胶(NR)中的应用.结果表明,随着HS-630用量的增加,胶料的门尼粘度和硫化特性变化不明显;硬度、定伸应力和耐磨性能显著提高;有效改善了胶料的耐热性能和耐臭氧性能;加入适量硅烷偶联剂改性的白炭黑后,并用胶具有更好的综合性能.
通过三维软件进行轨道减振器注射模具注胶系统、型腔系统、定位系统、排气系统及封胶系统等结构设计,将注射模具结构3D模型数据导入sigmasoft软件进行仿真分析,并修正流道结构,最终得出最优注胶系统,完成模具开发.结果表明,设计的Half瓣模结构借助注射机动力,实现了产品自动脱模,提高了生产效率.
Succinonitrile (SN)-based polymer plastic crystal electrolytes (PPCEs) have attracted considerable atten-tion as solid-state electrolytes owing to their high ionic conductivities similar to those of liquid elec-trolytes, excellent contacts with the electr
Magnesium hydride has been seen as a potential material for solid state hydrogen storage, but the ki-netics and thermodynamics obstacles have hindered its development and application. Three-dimensional flower-like TiO2@C and TiO2 were synthesized as the c
传统无源噪声整形SAR ADC因无源开关电容积分器有增益误差、相位误差而整形能力较弱.在无源噪声整形的基础上,文章设计了一种有源无源结合的噪声整形SAR ADC.该电路融合了低增益OTA和正反馈电路,仅增加少量功耗,基本消除了无源噪声整形模块的增益误差、相位误差.结果表明,该噪声整形10位SAR ADC的带宽为10 kHz,采样率为320 kHz,功耗仅109 μW,有效位数达15.6位.在-40℃～85℃、不同工艺角下,有效位数均超过15位.