【摘 要】
:
The surface morphology, cross-sections, and joint break force (JBF) of joints welded under different electrode forces were studied. The defects, such as electrode sticking, notch, and excessive expulsions, were observed in the joints. No desirable joints
【机 构】
:
National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology, Nancha
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
The surface morphology, cross-sections, and joint break force (JBF) of joints welded under different electrode forces were studied. The defects, such as electrode sticking, notch, and excessive expulsions, were observed in the joints. No desirable joints were achieved with the consideration of weld geometries and joint performances. From the cross-sectional morphology, the joint evolution during the RMW of Pt alloy and 316 LVM SS wires was developed, which involved cold collapse and heat promoted set-down of Pt alloy wire, unbalanced heating at interface, molten phase squeezed out, and defect formation. Finally, the defect formation was also discussed.
其他文献
In order to investigate the damage characteristic of ceramic-metal interpenetrating phase composite (IPC) under dynamic loading, uniaxial dynamic compression was performed to characterize the failure of SiC/Al composite with 15%porosity using a modified S
In order to further understand the wear mechanisms of cemented carbide cutter head of conical pick, six wornout cutter heads were investigated detailedly through scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). Abrasion wear an
Butt joints between Mg alloy AZ31B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31B Mg alloy and pure Al 1060 sheets were obtained. Intermetallic compound layer 1