The corrosion behaviors of a basic type of RE-containing magnesium alloy Mg-15Y processed by different heat treatment methods were studied in 3.5% NaCl solution at room temperature. The amount of Mg24Y5phase decreased with the extending of homogenization
【机 构】
：
School of Materials Science and Engineering, North University of China, Taiyuan 030051, China;State
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The corrosion behaviors of a basic type of RE-containing magnesium alloy Mg-15Y processed by different heat treatment methods were studied in 3.5% NaCl solution at room temperature. The amount of Mg24Y5phase decreased with the extending of homogenization treatment. The time for achieving dissolving equilibrium of homogenization treatment at 525, 535, and 545℃ was 24, 20, and 8 h, respectively. The corrosion behavior of Mg-15Y alloy was studied using immersion, hydrogen evolution and electrochemical tests. The experimental results revealed that the heat treatment improved the corrosion resistance, and the corrosion resistance became better with increasing the heat treatment time. The corrosion mode of the alloy after heat treatment was microgalvanic corrosion consisting of the cathodic Mg24Y5 phase and anodic α-Mg matrix, and Mg-15Y exhibited favorable uniform corrosion mode in NaCl solution. The volume and increasing tendency of the homogenization treatment samples were both more than those of the as-cast sample.
其他文献
An effective and reproducible preparation of silica sol nanospheres via a modified sol-gel process has been described. Monodisperse and stable silica sol nanospheres with uniformsize were successfully obtained through the optimized synthesis in which the
An energetic salt, sodium nitroformate (NaNF), was synthesized and characterized by elemental analysis, IR and UV spectra, and its crystal structure was first determined by single crystal X-ray diffraction. The structure exhibits two types ofπ-πstacking i
Ti2AlN/TiN functionally graded materials (FGM) were successfully fabricated by vacuum hot-pressing. Bulk density of the sintered samples was measured by Archimedes principle. The sample sintered at 1 300℃for 2 h has the maximum final density and lowest op
We researched the electric heating property from butyl rubber-loaded boron carbide composite. The effects of boron carbide content on bulk resistivity, voltage-current characteristic, thermal conductivity and thermal stability of boron carbide/butyl rubbe
The durability of silane-modified mortar, a cementitious composite, in acid rain environment was investigated given its extensive usage as a structural material. The results indicated that the addition of silane decreased the compressive strength of the c