Ti-23Nb-0.7Ta-2Zr-O (TNTZO, molar fraction, %) alloy is a newly developed multifunctional β-type titanium alloy. This alloy was reported to deform via a unique
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Ti-23Nb-0.7Ta-2Zr-O (TNTZO, molar fraction, %) alloy is a newly developed multifunctional β-type titanium alloy. This alloy was reported to deform via a unique dislocation-free deformation mechanism, and thus its recovery and recrystallization behavior should be further studied and compared with traditional BCC metals. The substructures of the cold-swaged and the annealed TNTZO alloy were investigated by transmission electron microscopy(TEM) to study the recovery of the cold-swaged TNTZO alloy.The results show that no dislocation can be distinguished from the cold-swaged TNTZO alloy due to the heavily-accumulated strains,whereas high density dislocations were observed in the cold-swaged TNTZO alloy after annealing at 800 ℃ for 5 min. During annealing, recovery proceeds through the redistribution and annihilation of the dislocations, which are considered to result from the plastic deformation and the recovery process of the cold-swaged TNTZO alloy is similar to that of ordinary BCC metals.
其他文献
提出了一种形式化的指令级并行程序执行模型(Instruction-Level Parallel Program Execution Model,ILPPEM).ILPPEM不仅可以描述程序实际执行过程的行为,也可以描述编译和执
以ＣＩＭＳ为代表的先进制造技术要求与之适应的产品信息模型的支持．产品信息包含结构化和非结构化两种形式．非结构化产品模型往往建立在异构环境之上，无法抽象成单一的数据库模式．目前对非结构化产品信息还没有形成合适的表达模型和相应的操作模型．提出的一个基于企业级异构环境下的非结构化产品信息的分布式模型，以ＳＧＭＬ／ＸＭＬ标准表达非结构化产品信息，其操作模型能在常规Ｗｅｂ／ＩＮＴＥＲＮＥＴ环境下方便地访问信
The glass forming ability of Gd-Co-Al ternary alloy systems with a composition ranging from 50% to 70% (molar fraction)for Gd and from 5% to 40% (molar fraction
Based on the available experimental information, the Ag-Si binary system was thermodynamically assessed using the CALPHAD method. The solution phases, including
Effect of activated carbon and electrolyte on electrochemical properties of organic supercapacitor was investigated. The results show that specific surface area
The crystal plasticity was implemented in the finite element method(FEM) software ABAQUS through the user subroutine UMAT. By means of discretizing the space at
The as-formed and post-deformed microstructures in both electroformed and spin-formed copper liners of shaped charge were studied by optical microscopy(OM), ele
This study investigated the rheological properties of semi-solid metal. An analytical model of apparent viscosity was built up based on analysis of energy dissi
Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions of Ni-39Ti-11 Si and Ni-42Ti-8Si (%, mole fraction, the same below), respectively, were fabricat
La2/3Sr1/3Mn1-xZnxO3 films (x=0.05, 0.1, 0.3, and 0.5) were prepared using magnetron sputtering method, and the effect of Zn doping on transport properties of t