Si/C/B powders were synthesized by carbothermal reduction of xerogels containing boride. Colorless,transparent and monolithic gel was obtained by using tetraeth
【机 构】
:
State Key Laboratory of Solidification Processing
论文部分内容阅读
Si/C/B powders were synthesized by carbothermal reduction of xerogels containing boride. Colorless,transparent and monolithic gel was obtained by using tetraethoxysilane,saccharose,tributyl borate,ethanol and distilled water as starting materials. When the xerogel was fired at 1 600 ℃ in the static argon atmosphere,the XRD pattern commences to show the crystallite peak corresponding with C. a-SiC was synthesized at 1 700 ℃,but amorphous remainders could not be eliminated completely. The XRD results show that the boron possibly enters into the silica network,leading to the formation of borosiloxane. Microstructure of a-SiC powders consists of agglomerated particles with diameters ranging from 30 to 100 nm. Though the samples prepared at 1 600 ℃ and 1 700 ℃ have better dielectric loss tangent than the sample at 1 500 ℃ due to exiting crystalline material,the dielectric constant and dielectric loss tangent of three samples reveal lower values.
其他文献
In functionally graded materials (FGM), the problem of interface stability caused by the volume deformation is commonly regarded as the key factor for its perfo
The annealed microstructures of the rolled AZ31 alloy sheets were examined by using light optical microscopy. The mechanical properties were measured by tensile
The magnetization, magnetostriction and compressive strengths of arc-cast polycrystalline and directionally solidified Tb0.36Dy0.64(Fe1-xMnx)1.9 (x=0, 0.05, 0.1
Besides the two phase transitions known in ferroelectromagnets, an additional transition was observed experimentally in Pb(Fe1/2Nb1/2)O3 and the possible mechan
One kind of novel reactive thermotropic liquid crystalline polymer-methacryloyl copolymer (LCMC) containing polyester mesogenic units was synthesized. Its struc
Novel ordered mesoporous Eu(DBM)3phen/APTES-SBA-15 (EAS) composites with reasonable photoluminescence property and interesting morphology of bundles of pearl-li
The electromagnetic pump imposes the electromagnetic motive force (Lorentz force) on the liquid metal directly and makes it move along the definite direction by
Epoxy resin was modified by multi-walled carbon nanotubes (MWCNTs) with an in situ method. The composite was observed using scanning electron microscopy (SEM) a
A super absorbent material was prepared with the super absorbent resin ( SAR ) and inorganicgel.The SAR of the carboxymethyl cellulose grafting acrylic acid ( C
SiC whisker reinforced MoSi2 composite powder was synthesized by a novel process,referred to the literature as chemical oven self-propagating high temperature s