【摘 要】
：
我厂生产的FA—B200型铣镗床中有一根φ14mm的钢丝绳,它的一个端头为锡钎焊接头,呈圆台状,长40mm,上端直径与钢丝绳外径相同,下端直径为φ24mm,如图所示。在焊接中我们采用
【机 构】
：
齐齐哈尔第二机床厂锻冶处,金属结构分厂 161005
论文部分内容阅读
我厂生产的FA—B200型铣镗床中有一根φ14mm的钢丝绳,它的一个端头为锡钎焊接头,呈圆台状,长40mm,上端直径与钢丝绳外径相同,下端直径为φ24mm,如图所示。在焊接中我们采用了灌制法并遇到了熔化的钎料流失和接头不易凝固的生产问题,为解决这一矛盾,我们选用烧制耐火砖用的粘土围护,很成功地完成了该件的焊接。现将焊接方法介绍如下。
The FA-B200 milling and boring machine produced by our factory has a φ14mm steel wire rope. One end of the wire rope is a tin brazed joint with a truncated cone shape and a length of 40mm. The diameter of the upper end is the same as that of the steel wire rope, and the diameter of the lower end is φ24mm. As shown. In the welding we used irrigation method and met the melted solder loss and the joint is not easy to solidification production problems, in order to solve this contradiction, we use the firebrick clay lining, it has successfully completed the pieces welding. Welding methods are introduced below.
其他文献
2016数字阅读大会以“创新·共享·绿色”为主题,是在“互联网+”和“大众创业、万众创新”背景下举行的一场盛会,展现出了会议组织以及数字出版产业观察和研讨的专业性。201
皮肌炎的临床表现多种多样,易误诊误治。作者通过对17例患儿病例分析,讨论其误诊原因。其中男7例,女10例。年龄～1岁1例,～5岁4例,～10岁8例,～14岁4例。入院前病程～3个月5例,～6个月5
本院泌尿外科从1980～1992年治疗先天性尿道下裂142例,两期手术58例,一期手术94例,其中膀胱粘膜尿道成形术74例;帽状包皮尿道成形术29例,阴茎皮肤带蒂皮管尿道成形术35例;阴囊
患者男性,7个月。因发热1天,伴呕吐、抽搐,发现皮肤瘀斑3小时于1990年1月8日入院。呕吐呈喷射性(5次)。足月顺产,母乳喂养,既往健康。体检:T38.5℃,P162次/分。R52次/分,昏
有人提出渗碳停炉两天以上,如再进行渗碳时,要进行渗罐处理。原因是:气体渗碳停炉后,随着温度的降低,大量氧化性气体进入炉内,马弗罐本身表面脱碳,产生微弱的氧化皮。这时,
患儿男性,48天,因“尿黄”而生食草鱼(约一斤左右)鱼胆1/3个,当晚出现发烧、腹泻,5～6次,黄色稀水样便,伴有非喷射性呕吐。体温:一般情况可,前囟平软,巩膜无黄染,心肺听诊正常
为了探索新生儿和高危新生儿β_2-m值及其临床意义,我们对49例正常新生儿和64例高危新生儿脐血β_2-m结果与新生儿体重、其母为高危妊娠及新生儿死亡的关系进行了初步探讨。
建国以来,我国脊髓灰质炎的发病数逐年下降,但1989年某些地区又出现了较大幅度的回升。在1988至1990的三年间,我们收治了13例脊髓灰质炎患儿,早期皆误诊为急性感染性多发性
进入新世纪的第一个春天,珠江两岸,花红树绿,生机勃勃。广东省老促会第四届全体理事大会于4月6日上午在广州举行。这是一次换届大会。300多位理事,冒着霏霏细雨,及时赶到,鱼
我院自1989年9月～1992年9月,应用自制胎肝(脾、胸腺)悬液(FLC),治疗格林—巴利综合征(GBS)12例,现报告如下:一、临床资料本组12例,男7例,女5例,年龄14～46岁,平均24岁。入院时