The effects of recrystallization on low cycle fatigue behavior were investigated on directionally solidified Co-base superalloy DZAOM.Optical microscopy and SEM were used to examine the mierostructure and fracture surface of the specimens.The mechanical testing results demonstrated that the low cycle fatigue property of DZ40M significantly decreased with the partial reerystallization.Fatigue cracks initiate near the carbides and the grain boundaries with slip-bands.Both the fatigue crack initiation and propagation can be accelerated with the occurrences of recrystallized grain boundaries.