论文部分内容阅读
采用三维晶体取向分布函数(CODF)法研究了循环相变α→β→α对工业纯钛的织构和屈服强度各向异性的影响,结果表明,经3次循环相变处理后,退火织构基本上被抑制了,形成了的纤维织构,及(0002) 基面型织构。 原冷轧织构转变为部分或的纤维织构(ND为板面法向)。这些取向分布特征使钛板材具有较低的屈服强度各向异性。
The effects of cyclic transformation α → β → α on the texture and yield strength anisotropy of commercial pure titanium were investigated by three-dimensional crystal orientation distribution function (CODF) method. The results show that after three cycles of phase transformation, Structure is basically inhibited, the formation of fiber texture, and (0002) Basal texture. The original cold-rolled texture is transformed into partial or fibrous texture (ND is normal to the plate surface). These orientation distribution characteristics make the titanium plate have lower yield strength anisotropy.