The structure and thermal parameters of Ni20Pd80 alloy were studied by X-ray diffraction(XRD). The diffraction experiments performed in the temperature range of 308–1100 K revealed that the alloy formed a face centered cubic (fcc) A1-type structure. The temperature dependence of the lattice parameters was investigated by using the Bragg line displacement method showing that the lattice parameter increases with the increase of temperature. The mean linear thermal expansion (MLTE(%)), coeffcient of thermal expansion (CTE, α), the characteristic Debye temperature (ΘD) and mean square amplitudes of vibration were determined from XRD data. The value of Debye temperature was found to be 253 K. It was found that temperature factor was independent of the static displacements.
The structure and thermal parameters of Ni20Pd80 alloy were studied by X-ray diffraction (XRD). The diffraction experiments performed in the temperature range of 308-1100 K revealed that the alloy formed a face centered cubic (fcc) A1-type structure. The temperature dependence of the lattice parameters was investigated by using the Bragg line displacement method showing that the lattice parameter increases with the increase of temperature. The mean linear thermal expansion (MLTE (%)), coeffcient of thermal expansion (CTE, α) Characteristic Debye temperature (ΘD) and mean square amplitudes of vibration were determined from XRD data. The value of Debye temperature was found to be 253 K. It was found that temperature factor was independent of the static displacements.