Fe-3Cr-0.5Mo-0.3C and Fe-3Cr-1.4Mn-0.5Mo-0.367C sintered alloys were plasma nitrided at different temperatures. Characterization was performed by microhardness
【机 构】
：
Department of Materials Engineering,School of Engineering
论文部分内容阅读
Fe-3Cr-0.5Mo-0.3C and Fe-3Cr-1.4Mn-0.5Mo-0.367C sintered alloys were plasma nitrided at different temperatures. Characterization was performed by microhardness measurement, optical microscopy, SEM and XRD. Both materials had similar nitriding case properties. 1.4% manganese did not change the as-sintered microstructure considerably.It was observed that monophase compound layer, γ, formed with increasing temperature. Compound layer thickness increased with increasing temperature while nitriding depth increased up to a level and then decreased. Core softening was more pronounced at higher temperature owing to cementite coarsening.
其他文献
“真是山在城中，城在水中，人在画中……”环信阳的泖河游览一圈，不少游客都这么感叹。
现结合公司应用实例,重点讨论如何提高通用电机变频的使用,针对其存在的问题进行简要分析,并提出相应地解决措施.
采用超声波辅助提取红景天中多酚类物质,在单因素实验基础上,通过正交试验优化了提取工艺条件.结果表明,最佳提取工艺条件为:料液比1:16(g/mL)、乙醇浓度50%、超声波提取时间
目的 了解急性乙型肝炎(AHB)患者感染HBV基因耐药相关变异性,并对变异相关因素HBV DNA、HBeAg、ALT、AST及TBil进行分析.方法 收集AHB患者123例,提取血清HBV DNA对反转录酶(R
目的:探讨针灸配合适宜技术对神经根型颈椎病的治疗效果.方法:对入住我科的神经根型颈椎病患者,按入院先后排序的奇偶数分为观察组和对照组各30例.均以针灸为主要治疗方法,对
目的通过白细胞介素1受体拮抗蛋白(IL-1Ra)间接体内转基因治疗实验性兔骨关节炎,探讨IL-1Ra对关节软骨病理改变及软骨基质降解的抑制作用.方法将30只新西兰大白兔随机分成3组
利用分子生物学技术,建立了一种快速、准确、实用的养殖对虾白斑病和斑节对虾杆状病毒的PCR检测方法,通过特异性试验和敏感性试验,并经测序,其PCR产物与目的基因符合率为99%,
以氧化剂 (NH4) 2 S2 O8为淀粉降解试剂 ,研究了降解条件与淀粉 /丙烯酸类单体接枝共聚反应的关系。结果表明 :当氧化剂 (NH4) 2 S2 O8用量为 1 .0 g、降解反应温度为 95℃、
Amorphous carbon nitride thin films were prepared by plasma-enhanced DC magnetron sputtering using twinned microwave electron cyclotron resonance plasma sources
空间钢构架是由横向和斜向缀条与纵向弦杆焊接而成的承重轻钢结构,将空间钢构架替代传统钢筋混凝土结构中的绑扎钢筋骨架,形成空间钢构架混凝土结构.为了研究空间钢构架混凝