Microstructure Evolution of AS41 Magnesium Alloy Fabricated by Ultrasonic Vibration
【机 构】
:
The Key Laboratory of Electromagnetic Processing of Materials,Ministry of Education,Northeastern Uni
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年5期
其他文献
The behavior that different magnetic treatment directions induce various amounts of welding residual stress reductions in low alloy steel was studied.Reductions of 26%-28% in the lon-gitudinal stress σ_x were obtained when low frequency alternating magnet
Relationship between leucite content and compressive strength of K2O-Al2O3-SiO2 sys-tem dental glass ceramics were investigated. 10 groups of feedstock powder with different composi-tions were treated according to the same thermal treatment system of leuc
The elastic microstrains in a crystallite of electrodeposited nanocrystalline copper were investigated by analyzing the high resolution electron microscopy(HRTEM)image.The mi-crostrain was considered as consisting of two parts,in which the uniform part wa
Nano SiO_2/NR composites were prepared through blending nano SiO_2 emulsion with natural rubber latex and then concreting with acetic acid.The emulsion nano SiO_2 was prepared with Na_2SiO_3·9H_2O and hydrochloric acid under the reaction of the assistant
Highly crystalline orthorhombic Bi_2WO_6 powders were hydrothermally synthe-sized from aqueous solutions of Na_2WO_4·2H_2O and Bi(NO_3)_3·5H_2O over a wide range of pH.The effect of pH on morphologies,sizes and properties of the Bi_2WO_6 crystals was inve
Biphasic calcium phosphate (BCP) powders were prepared by hydrolyzation proc-ess and surface-modified by directly grafted L-lactide (LLA) onto the surface of BCP through a chemical linkage. The grafting ratio of organic groups was 9 wt%. After surface mod