The bioleaching of a marmatite flotation concentrate with a moderately thermoacidophilic iron-oxidizing bacterial strain (MLY) is influenced significantly by te
【机 构】
：
Institute of Environmental Engineering,Institute of Processing Engineering
论文部分内容阅读
The bioleaching of a marmatite flotation concentrate with a moderately thermoacidophilic iron-oxidizing bacterial strain (MLY) is influenced significantly by temperature, pH, particle size, pulp density of ores and bacterial strains. Under such leaching conditions as the initial pH value of 1.5, temperature of 50 ℃, pulp density of 5%, particle size less than 35.5 μm (over 90%) and inoculating the adapted strains of MLY, the leached Zn is over 95% after 10 d of bioleaching. SEM observations show the cell attachment and the surface features of solid residues under different leaching conditions. XRD and EDX analyses show that a mass of elemental sulfur form during the bioleaching process. The technological feasibility of a microbiological process using MLY for extracting zinc from the marmatite concentrate is demonstrated.
其他文献
Used for industrial process with different degree of nonlinearity, the two predictive control algorithms presented in this paper are based on Least Squares Supp
A kind of conductive and heating unit, which can reach a high surface electroheat temperature at a low voltage, was developed in view of the traditional electro
The VCp reinforced stainless steel composite was produced by in-situ reaction casting. The composite was tested for its wear resistance under the wet abrasive c
Maximum bubble pressure measurement was employed to evaluate surface tension of Sn-8Zn-3Bi(0-0.15)Nd and Sn-8Zn-3Bi-(0- 0. 15)La solder melts. Wetting balance m
The gas atomization is the process that a liquid mass is disintegrated into a collection of liquid melt droplets by the impact of high velocity gas stream and s
Long afterglow phosphors MAl2O4:Eu2+, Dy3+ (M=Ca, Sr, Ba) were synthesized by microemulsion method, and their crystal structure and luminescent properties were
The influence of double aging on the microstructure and mechanical properties of ultrahigh strength steel Aermet 100 was analyzed. Under the double aging, there
An effective ensemble should consist of a set of networks that are both accurate and diverse. We propose a novel clustering-based selective algorithm for constr
An AZ61 alloy was subjected to hot compression at temperatures ranging from 523 K to 673 K,with strain rates of 0. 001 - 1 s-1. Flow softening occurs at all tem
Mixed Al-Si, Al-Si-SiC and Al-Si-W powders were employed as insert layers to reactive diffusion bond SiCp/6063 MMC. The results show that SiCp/6063 MMC joints b