【摘 要】
：
From a point of rheology, a novel method was proposed to evaluate the wet-spinning processability of acrylonitrile (AN)-acrylamide (AM) copolymers used for carbon fibers. The rheology behaviors of AN-
【机 构】
：
Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Southe
论文部分内容阅读
From a point of rheology, a novel method was proposed to evaluate the wet-spinning processability of acrylonitrile (AN)-acrylamide (AM) copolymers used for carbon fibers. The rheology behaviors of AN-AM copolymers were characterized by the rheometer. It was found that viscosicelasticity properties of solutions were changed with the introduction of AM comonomer. As the increase of AM content in the feeding, the viscosity of solution changes slightly, but the stability to time is decreased and the elasticity is increased. This indicates that the introduction of AM comonomer is not benefit for the wet-spinning process. According to the present study, the optimum AM content in the feeding should be lower than 1wt％.
其他文献
The goal of the present study was to evaluate the influence of mesophases addition on the resulting mechanical behavior and thermal conductivity of a carbon/carbon composite. The reinforcement was an
活性炭纤维富含微孔，具有结构不规则性和能量不均匀性，可以用分形维数来进行定量描述。分形维数的测量方法有吸附法、X射线小角散射法以及电镜分析的方法等。本文用吸附法探讨了活性炭纤维的分维。在77K下得到活性炭纤维的氮气吸附等温线(相对分压0～1)，用FHH方程计算得到分维：在室温大气压下得到有机蒸气(氮气为稀释气)在50～1000ppm的等温线，用特徵吸附能资料计算得到分维。将两者得到的结果进行了比较
磁控溅镀法已被研究用於当作大量制造PEMFC电极的工具，且相较於油墨式电极，其效能及触媒使用效率都有明显改善.本实验以磁控溅镀的方式来制作质子交换膜燃料电池之碳电极的Pt触媒层，并研究基材的变化对所制成之Pt薄膜碳电极的影响。实验中分别使用场发射枪扫描式电子显微镜舆高解析比表面积分析仪来观察基材的表面型态以及其比表面积，而由试片所组成之燃料电池的放电效能则是利用燃料电池性能分析系统来量测。实验中所
In this paper, several kinds of silver supporting activated carbon fibers (ACF) were prepared by the reduction adsorption of ACFs. The ACFs, using sisal fiber, viscose fiber, and pitch fiber as precur
活性炭纤维的孔隙结构形成於岌纤维的活化阶段，因而对於同一原料来讲，不同的活化方式决定了活性炭纤维的孔隙结构。本文中，以各向同性沥青炭纤维为原料，分别采用直接水蒸气活化(直接活化)以及不同(铁，钴)金属化合物浸泡後水蒸气活化(催化活化)和水蒸气再次活化(再次活化)的方式获得活性炭纤维。采用N2吸附法表徵了活性炭纤维的孔隙结构，考察了活化方式对孔隙结构形成的影响。结果表明，单纯采用水蒸气活化所得活性炭
In this paper, a conductive polymer composite was fabricated by the in-situ polymerization of styrene (PS) filled with multi-walled carbon nanotubes (MWCNT). The percolation behavior of the MWCNT/PS c
中钢碳素化学公司为以煤化学为主体的化学产业，并逐步迈入精密材料的领域。目前已顺利完成煤焦油蒸馏工厂之运作及产品之销售管道。中碳公司除持续研发符合市场需求的技术与产品，同时积极寻求合作项目，以期建立以煤焦油事业为核心，碳材料及特用化学品为双主轴的材料供应中心。目前介相碳微球生产能力80MT/年，本年度(2003)6月新产线投产後可违200MT/年的生产规模，现虽已建立自主碳/石墨材料分析检验技术，中
活性碳纤维具有大量的比表面积，是为一相当优异的吸附材料。而活性碳纤维在工业上常应用於触媒载体，藉由微孔洞关口处分布的官能基团可对触媒微粒进行吸附，触媒即可均匀分布於活性碳纤维表面，其承载密度亦高，催化效率也可因此提升。本实验即是以活性碳纤维浸染硝酸钴盐类，在化学气相沈积法中合成奈米碳纤维.过渡金属触媒是以硝酸盐类在氢氯气氛还原而得，触媒的粒径分布可利用活性碳纤维孔洞舆官能基的吸附作用来控制大小.实
采用溶胶-凝胶工艺，通过柠檬酸络合法制备NiZnCo铁氧体纳米晶，并使其均匀地分散到膨胀石墨基体中.通过这种方法，将本身为反磁性的石墨材料改性为一种兼备良好导电性和亚铁磁性的石墨基复合材料，进而研究了这些石墨基复合材料的物相组成、微观结构以及电磁性能。实验结果表明，磁性添加剂改善了复合材料的磁性能，提高了材料的磁损耗.垓材料可望用於各种需要防护电磁波干扰(EMI)的场合.
奈米碳管具有优良之电子场发射特性，利用网印法制备奈米碳管电子场发射体具有低成本、制程快和大面积制作等优点，因而使场发射平面显示器的未来发展颇受看好，但网印法有电子发射不均的严重缺点，因此解决这个问题将有助於大面积，低价格平面显示器的制作。本实验发现将场发射源材料阵列化，可有效解决电子发射分布不均的现象，且可提升场发射电流，经二极式场发射量测结果，阵列化後的电流密度由1.7～3.8 mA/cm2增加