【摘 要】
：
In order to account for the plastic surface deformation occurring in cold rolling,a novel,3-D Stribeck curve is proposed.This curve is characterised by three anchor points which represent(1)the fricti
【机 构】
：
Research Scientist,Quaker Chemical,The Netherlands
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
In order to account for the plastic surface deformation occurring in cold rolling,a novel,3-D Stribeck curve is proposed.This curve is characterised by three anchor points which represent(1)the friction in the boundary regime,(2)the friction in the elastohydrodynamic regime,and(3)the friction experienced in a thin lubricant film.Two operational numbers define the lubrication regime,representing(1)film formation in the inlet zone,governed among others by the process speed and(2)in-bite film formation facilitated by plastic surface deformation,governed among others by the sliding speed in the contact.Lubrication in the rolling process can be influenced by any of the 3 anchor points and 2 film formation mechanisms,all of which are influenced by the lubricant composition.The ideas behind the 3-D Stribeck curve can be used in a more targeted lubricant development.The 3-D Stribeck curve can be measured in the laboratory,preferably for emulsions.Additional test methods were developed to investigate boundary lubrication of emulsions under severe conditions,mimicking frictional power intensity and flash temperatures in the roll bite.Good correlations are found with performance in a pilot mill and a production mill.
其他文献
通过正交实验和固溶实验,研究了热处理工艺对KT5331钢组织和低温冲击韧性的影响规律。实验结果表明,热处理态试验钢显微组织均为回火马氏体组织,断口机理为穿晶解理断裂。1040～1120℃淬火温度对低温冲击韧性影响较大,并且随淬火温度升高,低温冲击功先上升后下降。当淬火温度低于1080℃时,低温冲击值较低是由原始奥氏体晶粒出现明显晶粒异常长大现象导致,当淬火温度高于1080℃时,低温冲击值下降是由原
针对钢铁行业发展面临严峻的成本挑战的现状,选择高性价比的铁矿粉对于降低炼铁成本至关重要.传统的铁矿粉性价评价方法主要有铁矿粉品位吨度价法、综合品位吨度价法、特殊成分价格折算法等,这些方法难以全面、准确地表征铁矿粉对于整个高炉炼铁系统有效的适应性;基于此,本文提出一种基于“铁矿粉-烧结-高炉炼铁”工艺流程模拟计算的铁矿粉性价评定方法,该方法综合考虑铁矿粉的价格、品位、脉石成分及其他特殊成分组成等因素
Although softening/melting tests are widely used to assess ferrous material properties in the cohesive zone of a blast furnace,there is little understanding of the mechanisms causing the softened bed
锅炉压力容器和压力管道等特种设备主要由管状承压类构件组成.由于该类设备始终处于高温、高压、冲刷及磨蚀等低周高应运行工况,其失效形式多种多样.再加上设计、制造、安装、使用、维护、修理与改造等各环节中难以避免地存在各种问题,因此,其失效原因分析往往变得更为复杂.为了分类总结30年来该类管状特种设备的技术与管理经验,文章针对短期超载超温失效,从断口金相与显微金相、宏观断口与微观断口形貌、SEM/TEM、
The reactivity of ferro-coke is much higher than the conventional coke and its application to the blast furnace is expected to improve the blast furnace reactions efficiency and to reduce fuel consump
A transient 3D mathematical model has been developed for the motion of inclusions in a continuous casting tundish with channel type induction heating.The Euler-Lagrange approach was employed,and the i
The production of Nb microalloyed coils by thin slab casting and direct rolling(TSDR)technologies shows some metallurgical characteristics that significantly differentiate this process from convention
本文介绍了一种高效全自动炼钢、炼铁炉渣分析技术,该技术实现了一条生产线四种炉渣自动无相互干扰的分析。通过将炉渣样品的全自动分析过程拆分为样品传递、样品破碎、样品研磨、样品压片等8个环节,找到了可能影响全自动压片成功率和炉渣交互污染的关键点位。利用实验设计的方法,确定了转炉渣黏结剂加入量0粒、研磨时间120 s、压片压力120 kN、保压时间10 s;确定了保护渣、精炼渣、高炉渣黏结剂加入量12粒、
随着高炉往大型化和长寿化发展,炉缸炭砖的重要性越发引人注目,但目前大高炉用炭砖还主要依赖进口.对于炉缸炭砖的质量,特别是左右炭砖寿命的抗铁水侵蚀等的重要指标方面,目前还没有特定用于大高炉炭砖的检测方法和标准.本文通过分析大高炉的工作特征,优化了高炉炭块抗铁水侵熔蚀性试验方法(GB/T 24201—2009)的测试条件,并对目前常用的多种炉缸用炭砖作了该项目的测试;通过将其测试结果和相对应的炭砖溶解
研究了回火温度对微观组织、力学性能以及低温冲击韧性的影响。结果表明:随着回火温度的升高,马氏体晶界及晶面逐渐有碳化物析出,组织中碳化物由片状连续不均匀分布变为颗粒状弥散分布;抗拉强度与屈服强度都随着回火温度的升高而下降,断面收缩率及断后伸长率随着回火温度的升高而增加;在350～450℃温度间,冲击功随回火温度升高稳定增加,回火温度在550℃以上时,冲击功呈急速升高状态,SCM435钢经油淬后在55