【摘 要】
：
Nucleation undercooling of non-magnetic metals like paramagnetic aluminum in high magnetic fields was investigated using the differential thermal analysis t
【机 构】
：
SchoolofMaterialsScienceandEngineering,ShanghaiUniversity,Shanghai200072,ChinaInstituteofElectricalE
【出 处】
：
第十一届全国固态相变、凝固及应用学术会议
论文部分内容阅读
Nucleation undercooling of non-magnetic metals like paramagnetic aluminum in high magnetic fields was investigated using the differential thermal analysis technique.It was shown that the nucleation temperature of pure aluminum decreased with increasing the magnetic field while the melting temperature was hardly changed.Based on the model of magnetic dipoles at the interface, it was found that the magnetic-field-induced interfacial tension contributed to the nucleation undercooling.The change in nucleation undercooling in the magnetic field was calculated, which was in agreement with experimental data.
其他文献
将纯铁(0.1mm)在640℃～680℃下气体渗氮,获得室温下稳定的穿透渗氮奥氏体.研究了Fe-N奥氏体晶界在225℃下等温转变的形貌和晶体学特征.晶界转变产物为板条状的γ/γ-Fe4N和α
金属钨具有高比重、高导热、低溅射产额等特性,然而,其在室温下韧性差,难以广泛应用；形状记忆合金在受载过程中发生应力诱发马氏体相变或去孪晶,且其具有高阻尼特性.根据
染料敏化太阳能电池是一种价格低廉、工艺简单、对环境友好的新型太阳能电池。然而染料敏化太阳能电池较低的转换效率严重制约了其应用与推广。本文采用脉冲电磁场辅助水
Co-Gd二元稀土共晶合金体系中,存在两个共晶合金Co-17.78wt％Gd和Co-81.45wt％Gd.虽然是同一二元体系的共晶合金,但其共晶组织完全不同,如图1和图2所示.稀土元素Gd的添加量不同,
激光选区成形技术(Selective Laser Melting)是快速原型及制造领域最具发展潜力的先进技术之一，尤其适合小批量、个性化、形状复杂的零部件生产。快速凝固Al-Fe-V-Si是一
单晶高温合金的激光修复过程中,为了保证单晶的完整性,需要避免CET的发生.对于给定的合金,激光熔池中的CET主要由温度梯度和生长速度控制[1].基体取向由于会显著的影响枝晶的
连铸坯柱状晶发达,大铸锭组织粗大,造成铸坯和铸锭宏观偏析严重,已经成为钢铁质量提升的瓶颈,至今国际上没有找到比较理想的解决方案.作者在揭示了脉冲电流细化金属凝固组织
液态金属因其独特的物理性能而在医疗器械、制冷工程及一些精密器件领域具有广泛的应用，其中GaInSn三元室温液态合金无毒环保，适合民用领域的推广而备受关注。本文通过DSC
将冷轧(多道次轧制、总变形量95％)+低回复退火后的0.12mm厚Al-Mn系铝薄板，在液氮中进行保温24h后发现了奇特现象：仅靠深冷处理就可促使铝薄板的粗大纤维晶粒裂解成许多准纳
在低于传统疲劳极限的循环应力下,高强钢仍可能发生疲劳损伤和断裂,相应的疲劳断裂周次在107以上(超高周).高强钢的超高周疲劳问题是疲劳研究的重要新领域.一方面,超高周疲劳