【摘 要】
:
Municipal solid waste incineration bottom ash (IBA) contains metallic aluminum which could generate hydrogen gas and lead to the occurrence of concrete crack when IBA is used in cement matrix.In this
【机 构】
:
Energy Research Institute@NTU (ERI@N), Interdisciplinary Graduate School, Nanyang Technological Univ
【出 处】
:
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
Municipal solid waste incineration bottom ash (IBA) contains metallic aluminum which could generate hydrogen gas and lead to the occurrence of concrete crack when IBA is used in cement matrix.In this paper,IBA was pre-treated with alkaline solution, i.e.sodium hydroxide solution or calcium hydroxide solution, under certain conditions.The alkali treatment effect on metallic aluminum removal, chemical composition of IBA,compressive strength as well as strength activity index (SAI) of cement-IBA mortar and heavy metal immobilization in IBA was presented.The results showed that metallic aluminum in IBA could be completely removed by treatment with sodium hydroxide solution, and the alkali treatment did not change the major components of IBA though some aluminum compounds changed.From the compressive strength of cement-IBA mortar, it showed some pozzolanic property of IBA could sacrifice when IBA is treated with alkaline solution.However, the SAI value of cement-IBA mortar using IBA treated with sodium hydroxide solution under low temperature and low PH can still reach more than 80%, which is meaningful in practical application.Alkali treatment can also benefit heavy metal immobilization in IBA.In general, this paper revealed a viable way to treat incineration bottom ash (IBA) to be suitable for supplementary cementitious material application.
其他文献
NanoSiO2 appears to be one of the most attractive nanomaterials for cement and concrete researchers, however dispersion of nanoSiO2 and excessive shrinkage induced by nanoSiO2 limit its effective use.
Through characterization techniques (XRD, TG / DTA, chemical analysis classical, 27Al and 29Si MAS NMR,Blaine, BET, granulometry laser) and tests of reactivity of metakaolin with calcium hydroxide (ca
Environmental concerns have prompted research into the use of carbon dioxide as a feedstock in the production of concrete.Industrial trials have examined the use of CO2 in ready-mix production.A gas i
The objective of this paper is to examine the rheological properties of cement paste with lower water-binder ratio (W/B) of 0.25.The electrochemical technique is utilized to assess the evolution of th
In this paper, the basic properties, including setting time, compressive strength, drying shrinkage of sulphate aluminum cement paste in corporating bamboo charcoal (BC)with the various fineness and c
Amorphous calcium aluminate/anhydrite is a unique cement1tious material that otters superior nydratlon acuv1ty compared with crystalline calcium aluminates.It is useful as a rapid hardening additive a
Polycarboxylate superplasticizer (PC) disperses cement particles mainly by steric hindrance effect.To clearify whether sulfates affect the dispersion capability of cement paste by weakening its steric
The effect of calcium chloride (CaCl2) on tricalcium silicate (C3S) hydration was investigated by Scanning Transmission X-ray Microscopy (STXM) with Near Edge X-ray Absorption Fine Structure (NEXAFS)
The reactive alumina, Al2O3r-, constituent of natural and artificial pozzolans, is a very important chemical parameter that is directly related to the durability of the resultant blended cements once
Steel industry generates two types of slags as by-products, namely iron making slag and steel making slag.The use of Iron making slag also known as BF slag as a constituent of concrete, either as an a