核壳结构的5V正极材料Li[(Ni0.5Mn1.5)0.5(Ni0.3Mn1.3Co0.4)0.5]O4的制备和应用

来源 :中国化学会第十七次全国电化学大会 | 被引量 : 0次 | 上传用户：loughtjiang

【摘要】

：

LiNi0.5Mn1.5O4是通过向LiMn2O4掺杂Ni得到的新一代高电压锂离子电池正极材料,其结构与LiMn2O4相似,为尖晶石结构.并当Ni代替部分Mn后,改善了Mn3+存在导致的LiMn2O4结构不稳定性,LiNi0.5Mn1.5O4具有高的能量密度、高的充放电平台、良好的倍率充放电性能以及低成本易于合成等优点,是正极材料中的研究热点.

【作者】

：

胡航朱继涛陈清波陈强陈红雨

【机构】

：

华南师范大学化学与环境学院,广东,广州,510006 深圳慧通天下科技股份有限公司,广东,深圳,5

【出处】

：

中国化学会第十七次全国电化学大会

【发表日期】

：

2013年2期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

Facile Method to Shift the Dirac Point of Graphene Field-Effect Transistors

Graphene is a one-atom-thick planar sheet of sp2-hybridized carbon atoms tightly packed in a two-dimensional honeycomb crystal lattice.It has many excellent properties, such as high mobility and adjus

会议

GrapheneFETsSigN4carrier concentration

Supercapacitors Based on High-Surface-Area Graphene

An improved Hummers method was used to the preparation of exfoliated graphite oxide(GO), and graphene with high-surface area was obtained after chemical reduction of GO by hydrazine hydrate.A stable s

会议

graphenespecific surface areaspecific capacitance

Direct Growth of Defsct-free Graphenes on Sapphire by Chemical Vapor Deposition

Graphene has attracted intense interest because of its superb properties, such as high mobility and optical transparency.Meanwhile, depositing graphene on appropriate substrates is one of the main obs

会议

GrapheneSapphireChemical Vapor DepositionRaman Spectroscopy

Facile Preparation of carbon spheres/graphene composites for Supercapacitor

Supercapacitors have sparked enormous interest in the field of electrical energy storage devices due to their high power density, long cycle life, wide operating temperature range, and short charging

会议

carbon spheregraphenecompositesupercapacitor

Synthesis and electrochemical properties of graphene-modified LiCo1/3Ni1/3Mn1/3O2 cathodes for lithi

Previous investigations indicate that graphene can be used to effectively improve the electrochemical performance of LiFePO4 cathodes.LiCo1/3Ni1/3Mn1/3O2 (LCMNO) is a much more attractive cathode, and

会议

GrapheneLiCo1/3Ni1/3Mn1/3O2modified

The use of graphene oxide membranes for the softening of hard water

Strong chemical interactions between the oxygen-containing functional groups on graphene oxide (GO) sheets and divalent metals ions were exploited for the softening of hard water.GO membranes were pre

会议

Graphene oxideMembranesHard waterSoftening

Li4Ti5O12/graphene nanostructure for lithium storage with high-rate performance

Li4Ti5O12 with good crystallization and nanometer-size (18 nm) was in-situ grown on monolayer graphene (2 nm) using OmimCl as exfoliated agent.Such Li4Ti5O12/graphene nanostructure exhibits excellent

会议

Li4Ti5O12GrapheneIonic liquidAnode materialsLithium ion battery

Reduced graphene oxide/ordered mesoporous carbon nanospheres composites used as supercapacitor elect

Graphene based carbon materials are promising electrodes for supercapacitors due to the high surface area, great conductivity of graphene, and remarkable chemical stability of the composites.In this p

会议

reduced grapheme oxideordered mesoporous carbon nanospheresupercapacitorspeci

P-phenylenediamine functionalized graphene oxide for high performance supercapacitors

P-phenylenediamine (PPD) functionalized graphene oxide (GO) materials (PPDG) were prepared through a one-step solvothermal process and their application as supercapacitors were studied.The structures

会议

graphenep-phenylenediaminesupercapacitor

固相法制备LiMnPO4/C及其电化学性能的研究

LiMnPO4/C materials were prepared by solid state reaction method by using traditional raw materials,surfactant-assisted precipitated NH4MnPO4·H2O as reactants respectively,and the structural and elect

会议

核壳结构的5V正极材料Li[(Ni0.5Mn1.5)0.5(Ni0.3Mn1.3Co0.4)0.5]O4的制备和应用

与本文相关的学术论文