The protection study of carbon steel corrosion induced by iron-oxidizing bacteria

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：june_jt

【摘要】

：

In this paper,the inhibition effect of a magneticfield(MF)and inhibitors on corrosion behavior of Q235 carbon steel induce by iron-oxidizing bacteria were studied using surface analysis,weight loss an

【作者】

：

Liu Hongfang LiuHongwei

【机构】

：

Hubei Key Laboratory of Materials Chemistry and Service Failure,School of Chemistry and Chemical Eng

【出处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年10期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

Effect of Molybdate and Organic Inhibitors on the Corrosion of Ductile Cast Iron

Carbon steel and ductile cast iron used in a closed cooling system may be corroded.In order to control this type of corrosion problem,corrosion inhibitors such as nitrite,silicate,molybdate,and hydraz

会议

Online asset management and operational optimisation through real-time integrity monitoring

This presentation will focus on monitoring the integrity of fixed equipment in the oil and gas industries,upstream and downstream.The insight gained from a real time understanding of asset integrity e

会议

Developing Novel Coatings for Impeding high temperature corrosion of solid oxide fuel cells intercon

Chromia forming ferritic stainless steels are the most acceptable materials for solid oxide fuel cell(SOFC)interconnects application because of their cost effectiveness and good oxidation resistance,a

会议

Effect of Pseudomonas on the degradation of coating in seawater

It is known that microorganisms degrade many materials.However,very little is known about the biodegradation of marine coatings.In this study,we explored the degradation of epoxy resin varnish coating

会议

Hydrogen-induced cracking susceptibility and hydrogen trapping efficiency of the welded X100 pipelin

X100 pipeline steel---a kind of high strength low alloy(HSLA)steels used for pipeline in the transportation of oil and gas that contain H2S are limited due to the mechanical and corrosion problems ind

会议

Electroless Plating of Ni-P Alloys with High P Content Based Compound Complexing Agents on Ternary

Single complexing agents cannot meet multiple demands including stability of bath,plating rate and quality of coating.Existing compound complexing agents arc either too expensive or unsatisfactory in

会议

The Application of Corrosion Monitoring Technology in Oilfield Wellhead

Serious corrosion occurs in the downhole and wellhead equipment and pipeline of an oilfield because of high water content in crude oil,high mineralization and high CO2 Content.

会议

The Application of FSM Technology in Refinery Units

The flash unit was designed according to low-sulfur and low-acid value crude oil in a petrochemical company.Except for pipeline material(12Cr5MoI)in flash furnace,the material of all pipelines is 20#

会议

Corrosion behavior of Cu-Ni-Al-Si-based alloy with super high strength

A novel Cu-Ni-Al-Si-based alloy with super high strength was designed.The microstructure evolution and corrosion behavior of the alloy have been investigated.

会议

Corrosion behavior of Sn-3.0Ag-0.5Cu lead-free Solder alloy under thin electrolyte layer containing

The corrosion behavior of Sn-3.0Ag-0.5Cu(SAC305)lead-free solder alloy under thin electrolyte layers containing 0.5 M NaCl has been investigated by electrochemical impedance spectroscopy(EIS),potentio

会议

The protection study of carbon steel corrosion induced by iron-oxidizing bacteria

与本文相关的学术论文