  5. Glass formation, physical and optical properties of chalcogenide glasses in novel ternary Ge-Sn-S sy

Glass formation, physical and optical properties of chalcogenide glasses in novel ternary Ge-Sn-S sy

来源 :The 24th International Conference on Glass( ICG Congress 201 | 被引量 : 0次 | 上传用户：i_love_snj
【摘 要】
：
Over the past few decades, chalcogenide glasses (GhGs) have been widely investigated due to a variety of technological application in infrared optics[1].As a well-known infrared transmitting material,
【作 者】
：
Yicong Huang Feifei Chen Shixun Dai Tiefeng Xu Qiuhua Nie 
【机 构】
：
Laboratory of Infrared Material and Devices, Ningbo University, Ningbo, Zhejiang 315211, China
【出 处】
：
The 24th International Conference on Glass( ICG Congress 201
【发表日期】
：
2016年11期
【关键词】
：
Chalcogenide glass Compositional dependencies Glass forming region Raman spectra 
下载到本地 , 更方便阅读
下载此文 赞助VIP
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
　　Over the past few decades, chalcogenide glasses (GhGs) have been widely investigated due to a variety of technological application in infrared optics[1].As a well-known infrared transmitting material, GhGs offer infrared transparency from visible up to the far infrared (FIR) region, covering the widely used atmospheric IR windows of 3-5 and 8-14 μm, which are very important to todays telecommunication.
其他文献
Fracture problem of a nonhomogeneity high temperature superconductor strip based on real fundamental
To analyze the fracture problem of the nonhomogeneity high temperature superconductor(HTS)strip under electromagnetic force,we derive the real fundamental solutions based on eigenvalue and eigenvector
会议
nonhomogeneity high temperature superconductorreal fundamental solutionssingul
Nano-structured glass ceramics for color tunable white LED color converter
Inorganic color converters such as phosphor ceramic (PC) and phosphor-in-glass (PiG) have been now commercialized to replace organic resin which suffered from weak thermal and chemical stabilities for
会议
2.7μm emission in oxy-fluoride glass ceramics containingLuOF∶ Er3+ nanocrystals
Er3+ doped transparent oxy-fluoride glass ceramics containing LuOF nanocrystals was prepared by traditional melt-quenching and subsequent thermal treatment method.The influence of thermal treatment te
会议
Oxy-fluoride glass ceramicsLuOF nanocrystals2.7 μm luminescence
Cordierite based nano microcrystalline glass
In order to get Nano-sized cordierite glass-ceramics, different kind of nucleation catalysts was tested in the cordierite base glass , such as TiO2, Zr2O3, and admixed TiO2-Zr2O3.
会议
cordieritenucleation catalystsheat treatmentnano microcrystalline glass
Vanadium phosphorus sealing glass crystallization stability of antimony-doped
80V2O5-20P2O5-xSb2O3 (VPS) (x =1, 3, 5 mol%) Glasses were prepared.The crystallization stability analysis of VPS glass were investigated.The effect of Sb2O3 on crystallization lower limit temperature
会议
Sb2O3vanadium phosphate glass51V Static NMRcrystallization stability
Phase separation and crystallization processes during nuclear glass synthesis
Nuclear waste glasses are produced by a succession of physical and chemical interactions between a solid waste (calcine) and a glassy precursor (glass frit) through a high-temperature vitrification st
会议
Phase separation in the Na2O-B2O3-SiO2-Fe2O3 glass-forming system
Adding Fe2O3 to sodium borosilicate (SBS) glass-forming system gives such glasses a number of valuable properties, which makes it possible to use them for producing semiconducting fibers, glass enamel
会议
Phase separation and the effect of B2O3 and P2O5 addition in RO-Al2O3-SiO2 system
The phase separation of glasses of the 17(CaO+MgO)-6Na2O-6AhO3-65SiO2-x(B2O3 +P2O5)(0 ≤ x ≤6) (wt%) series were investigated using DSC, XRD and SEM.The X-ray diffraction (XRD) and differential scannin
会议
Towards macroporous silica monoliths by phase separation and leaching of chemically modified sodium
Porous glasses are the products of phase separation and chemical leaching of glasses with a certain composition.Phase separation occurs, if glasses, whose compositions are within a "mixing gap" of a c
会议
Ho3+/Er3+ co-doped fluoride glass sensitized by Tm3+ pumped by a 1550 nm laser diode for efficient 2
In present paper, a high emission intensity of 2.0 μm is reported of Er3+/Ho3+ co-doped fluoride glass sensitized by Tm3+ ions under 1550 nm excitation.
会议