【摘 要】
：
The crystallization behaviors of homo-polypropylene and random co-polypropylene with or without β-nucleating agent were investigated comparatively by using differential scanning calorimetry (DSC), wid
【机 构】
：
Petrochemical Research Institute of PetroChina, Beijing 100195, China
【出 处】
：
Asian Polyolefin Workshop (APO2013)2013亚洲聚烯烃研讨会
论文部分内容阅读
The crystallization behaviors of homo-polypropylene and random co-polypropylene with or without β-nucleating agent were investigated comparatively by using differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WXD), and polarized optical microscopy (POM).
其他文献
Polypropylene (PP) is one of the most versatile thermoplastics, due to its well-balanced mechanical properties, easy processability, lightweight, low environmental load, and so on.1 Numerous studies h
The cycloolefin polymers (COPs) have attracted much attention due to their fascinating properties, such as high transparency, low water absorption, chemical resistance and so on.
Since chromium catalyst was firstly discovered in 1953[1,2], it can be divided into three kinds, which are Phillips catalyst, chromocene catalyst and organo-chromate catalyst[4].
Heterophasic copolymers of polypropylene (PP) containing dispersed ethylene-propylene random copolymers (EPR), known as impact PP copolymers (IPC), are an important sub-class of PP that are superior t
Copolymerization of 1,3-butadiene with (E)-l-phenyl-1,3-butadiene (1PB) was investigated in a large range of 1PB feed ratios (0～50 mol％) by using CpTiCl3/MAO catalyst.
In this paper, the performance of JHMGC 100S, a kind of HDPE for pipe, was studied, and the comparison with other typical PE 100 resin at home and abroad was also did.The results show that: the impact
Amidinate ligands are versatile and easily modified by variation of substituents on the conjugated N-C-N backbone to adjust the steric and electronic properties.1 In the similar way, we developed a cl
The dimethyl (pyridyl-amido)hafnium has an unprecedented performance in the generation of highly isotactic high molecular weight polymers, not only for propylene homopolymerization but also for its co
More than half a century after its discovery, the Phillips ethylene polymerization catalyst CrOx/Si02 is still responsible for up to half of current world high-density polyethylene production.1 Despit
Binuclear complexes in catalysis are of interest due to potential synergistic effects.1 Some attention has been paid to bimetallic complex pre-catalysts for ethylene reactivity and this has been discu