【摘 要】
:
The 3-D needled C/C preforms with different fiber volume fraction, by chemical vapor infiltration (CVI) densified to obtain a density of 1.0 ~ 1.1g / cm3, w
【机 构】
:
College of Aerospace and Materials Engineering,National University of Defense Technology,Changsha 41
【出 处】
:
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
The 3-D needled C/C preforms with different fiber volume fraction, by chemical vapor infiltration (CVI) densified to obtain a density of 1.0 ~ 1.1g / cm3, were used to fabricate C/C-SiC composites by gaseous silicon infiltration (GSI).The research studied the effects of fiber volume fraction onthe phases and mechanical properties of C/C-SiC composites fabricated by GSI, and analyzed of reaction mechanism of Si and C.The results show that, although the SiC contentdecreaseas the fiber volume fraction increases,the residual Si content, porosity and the mechanical properties increases.
其他文献
To enhance application of ceramic matrix composites in engineering, a B/S database system was developed with interface for different CAX software.Data syste
Based on the CT scan results of 3D four-directional braided ceramic matrix composites and theoretical research, an improved 3D cell model was established.Th
In order to evaluate the thermal strength of ceramic matrix composite structures in engineering, the macro nonlinear constitutive model was developed based
The interphase play a role effect on the mechanical properties of composites.Especially for the Cf/SiC composites prepared by GSI process, the ideal interph
The carbon felt reinforced C/SiZrOC composites were fabricated with zirconium butoxide(ZTB), divinylbenzene(DVB) and polysiloxane(PSO) as precursors.The com
SiC nanowires exhibits unique properties such as high modulus of elasticity, high strength, low weight, high-temperature oxidation resistance, corrosion res
为推动陶瓷基复合材料在工程中的应用,并满足数字化设计需求,设计与开发了一个具有多种CAX软件接口的B/S架构数据库系统。根据陶瓷基复合材料的特点构建了材料数据体系,基于
超高温陶瓷材料暴露于极端高温飞行环境中会导致其发生氧化,表面生成的氧化物具有不同的热物性从而对传热过程造成影响。针对预氧化的ZrB2和ZrB2-SiC材料,基于氧化模型预测
高超声速飞行器不断发展使飞行器表面面临愈加恶劣的热环境,传统耐温隔热材料已难以满足需求.SiCO体系中的B元素在高温处理过程中会形成BCXO3-X结构,该结构能够打乱体系中
ZrB2具有优良的物理特性和化学稳定性而应用于许多领域,为了改善ZrB2难以烧结致密化和高温易氧化,本文通过共沉淀法制备包覆式Al203-Y203/ZrB2复合粉体,并对其进行放电等离