【摘 要】
：
The silver doped TiO2 sol is prepared through Sol-Gel method, Ti(OC4H9)4 and C2H6OH are materials, AgNO3 is the component for inducting silver ion.The inorganic film is formed on glass through dipping
【机 构】
：
Department of Biochemical and Chemical Engineering, Zhejiang University of Science and Technolohy, H
【出 处】
：
2014中国溶胶-凝胶学术研讨会暨国际论坛
论文部分内容阅读
The silver doped TiO2 sol is prepared through Sol-Gel method, Ti(OC4H9)4 and C2H6OH are materials, AgNO3 is the component for inducting silver ion.The inorganic film is formed on glass through dipping-draught, under the dropping rate 6crn/min.the temperature of heat treatment is 500℃.According to the data of XRD and SEM, discovered the TiO2 film exist as titania in a great measure.The diameters of the TiO2 particles in the coatings are in the range 50-100nm.According to the experiment of antibacterial test using escherichia coli, the antibacterial mode of silver is by contact, and only a little silver doped film can get good antibacterial property.The transparency of the glass coated with TiO2 in visible spectra is high and its transmissivity compared with common glass is over 65%.
其他文献
以锡酸钠和尿素为原料，采用水热法和原位化学还原法分别制备出SnO2空心球表面载有银纳米颗粒的Ag/SnO2复合粉体，通过X射线衍射(XRD)、扫描电子显微镜(SEM)、能谱仪(EDS)、透射电子显微镜(TEM)等研究了表面银颗粒的厚度及分布均匀性。结果表明，两种方法均能制备出平均粒径为1～2 μm、分散性良好的空心微球；水热法一步合成制备的SnO2空心球表面银颗粒细小且有团聚现象，而采用原位共沉淀
以氨水为沉淀剂,EDTA+草酸为组合胶凝剂,采用化学共沉淀法成功合成了高纯单一相锡酸镧(La2Sn2O7)粉体；并采用氧化还原法、光催化反应、高能球磨工艺对锡酸镧粉体进行表面载银工艺研究。通过附带能谱仪的扫描电子显微镜(SEM/EDS)与X射线电子衍射(XRD)对其形貌及物相进行相应的表征。结果表明：上述三种不同载银工艺都能够合成复合颗粒态、物相纯度较高的Ag-La2Sn2O7复合粉体；其中,以葡
In this work four different methods are utilized to synthesis Ag/ZnO composites, including the solid phase crystallization method, the precipitation method, the silver mirror reaction method and the h
The morphology and properties of Ag-SnO2 composites by electroplating method were discussed.The morphology, physical properties and silver-to-stannic dioxide boning of Ag-SnO2 composites by electropla
高放射性废物(HLW)中锕系核素(Np,Am, Cm)对生物圈有着极大的危害,严重的限制了核工业的健康持续发展.目前,对高放射性废物进行有效处置的方式有:玻璃固化、陶瓷固化和玻璃陶瓷固化[1].玻璃固化是目前实际解决此问题最常用的方式之一,其中短期玻璃浸出性能表现良好,但理论上玻璃属于亚稳态,在长期地质处置的稳固性,仍需深入考察[2].
人类在合理开发和利用核能过程中,不可避免地产生大量放射性废液,这类废物对环境构成了一定的潜在危害.气凝胶是一种高比表面积、高孔隙率的材料,孔道结构的存在有利于吸附重金属核素[1],用气凝胶对含锕系元素的放射性废液进行吸附固化处置,是一种便捷、安全、廉价的方法.SiO2-ZrO2复合气凝胶与单一成分的SiO2气凝胶和ZrO2气凝胶相比,拥有许多优越的物理化学性能[2].
Nanocomposites based on modified BaTiO3-Dy2O3 nanoparticles filled poly (vinylidene fluoride) polymer have been prepared.Comparison of two different dispersion mediums (ethanol and isopropanol) in sol
以NiCl2·6H2O和SnCl4.5H2O为原料,采用水热法制备了Ni掺杂SnO2纳米粉体,采用TG-DTA、XRD、SEM、EDS等手段,考察了前驱体Ni的掺杂量、煅烧温度等参数对所得纳米粉体物相、晶粒度、形貌等的影响.结果表明：当前驱体中Ni2+与Sn2+摩尔比为1∶5,水热温度为160℃时,Ni掺杂SnO2粉体分散性较好、颗粒均一度高,平均尺寸约200nm；随着Ni掺杂量增加,SnO2特征
以化学Ag粉、纳米SnO2为原料,用高能球磨法制备复合粉体并通过粉末冶金、热挤压等工艺获得Ag/SnO2线材并对其进行退火.采用扫描电镜(SEM)、X射线衍射仪(XRD)、拉伸试 验机、电桥以及电寿命试验机等对线材电寿命测试前后的组织结构、机械和电学性能进行表征.结果表明,热挤压后线材的密度增至10.0 g/cm3,氧化物沿挤出方向呈纤维状分布.随着退火温度的升高,线材的电阻率由2.432 μΩ.
采用密度泛函理论方法研究了Au10团簇催化CO氧化反应的详细机理.对CO、O2、O、CO2四种主要吸附物及CO+O2、 CO2+O、CO+O和CO+O+O四种共吸附物的吸附行为进行计算,得到最佳活性吸附位.模拟反应分别按照Langmuir-Hinshelwood(LH)机理和Eley-Rideal(ER)机理进行,其中LH机理包括L1、L2两条路径,ER机理包括E1、E2两条路径.通过对各路径活化