Structural origin of mixed modifier effects in silicate glasses

来源 :The 24th International Conference on Glass( ICG Congress 201 | 被引量 : 0次 | 上传用户:qiuyujie
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  As one of the most challenging problems in oxide glasses, structural origin of the so-called mixed modifier effect,which refers to non-additive changes of certain performances when one modifier species is substituted by another keeping the total modifier content constant, is still not fully understood despite much progress in the past few decades.
其他文献
Physical Vapour Deposition (PVD) processes are usually conducted under vacuum and involves physical processes, however in the special cases, the film forming process could involve some chemical reacti
会议
Cation migration according to a voltage gradient can be applicable to the fine pattern formation on glasses below their glass transition temperature (Tg), which is called as "electrical nanoimprint (E
会议
Nowadays, there is a wide selection of refractory materials that could be used for construction of glass furnaces.There are some materials suitable for direct contact with molten glass.
会议
This paper will demonstrate how Furnace Design & Control can increase the overall glass furnace efficiency by utilizing advanced furnace modeling to help select the most-optimal furnace design for a c
会议
Electrical melting technology was developed quickly in China and abroad.There were more than 100 all-electrical melting furnace built in a variety of industries.
会议
Chromium oxide refractories have been used for many years in the glass industry for their superior resistance to corrosion.In E glass furnaces, chromic oxide is required in most glass contact areas be
会议
Silicon (SiO2), boron (B2O3) and sodium (Na2O) oxides are the main components of the industrial radioactive waste confinement glass (French R7T7 glass).In order to characterize its physicochemical pro
会议
The electronic structure, network bonding, optical excitation, electron localization, elastic constants and mechanical properties of a larger continuous random network (CRN) model of amorphous SiO2, G
会议
It has been reported that certain members of the zeolitic imidazolate framework (ZIF) family can be melted and vitrified under optimal synthetic and thermal conditions.1 For instance, ZIF-4 [Zn(C3H3N2
会议
Chalcogenide glasses (ChGs) in the As-Se system possess good stability against crystallization and a wide transparency in the infrared domain which have made them the higher technological importance i
会议