通过晶间腐蚀和点蚀等多种腐蚀试验方法,研究了含碳量对304型不锈钢局部腐蚀行为的影响。试验结果表明,超低碳不锈钢具有更好的抗晶间腐蚀与抗点蚀性能。
Through the intergranular corrosion and pitting corrosion and other corrosion test methods, the effect of carbon content on the corrosion behavior of 304 stainless steel was investigated. Test results show that ultra-low carbon stainless steel has better resistance to intergranular corrosion and pitting corrosion resistance.