A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and the
Knowledge of the mechanical properties of two-component parts is critical for engineering functionally graded components. In this study, mono-and two-component