Preparation and Characterization of a Magnetic Binary System Comprise of γ-Fe2O3and α-FeO(OH)Nanopar

来源 :2015中国国际功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户：down222

【摘要】

：

Magnetic nanoparticles were prepared from a low crystalline ferrihydrite(Fe5O7(OH)· 4H2O)precursor by a chemically-induced transformation method using mixed FeCL/NaOH solution.

【作者】

：

Xiao-min Gong Jian Li Jun-ming Li Hong Mao

【机构】

：

School of Physical Science and Technology,South west University,Chongqing,China

【出处】

：

2015中国国际功能材料科技与产业高层论坛

【发表日期】

：

2015年2期

【关键词】

：

Ferrihydrite Maghemite Goethite Nanoparticle

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Magnetic nanoparticles were prepared from a low crystalline ferrihydrite(Fe5O7(OH)· 4H2O)precursor by a chemically-induced transformation method using mixed FeCL/NaOH solution.

其他文献

Polymeric Composite Containing High Performance Shear Thickening Fluid

Shear thickening fluid (STF) is concentrated colloidal suspensions composed of non-aggregating solid particles suspended in fluids.

会议

Evaluation of X-ray Transmittance for Carbon Fiber Composite for the Table of Computed Tomography

Since the early 2000s, composites have been applied to medical device components.Nowadays, they are also being used to satisfy X-ray transmission performance requirements and to take advantage of thei

会议

Radiant Protective Performance of Aluminized Fabrics in Fire Proximity Suit

Rely upon the ability to reflect more than 90％ of radiant heat, aluminized fabrics are widely used in fire proximity suit to protect against intense radiant heat during proximity fire fighting.In this

会议

Novel pH-sensitive poly(vinyl alcohol)based polyampholyte as pervaporation membrane

Sodium acrylate(NaAA)and acrylamide(AM)were grafted onto poly(vinyl alcohol)(PVA)using potassium persulfate as an initiator.Graft copolymerization namely poly(vinyl alcohol)-g-poly(acrylamide/sodium a

会议

Poly (vinyl alcohol)PervaporationPolyampholyteIsoelectric pointDehydration

High Temperature Tribological Properties of Plasma Sprayed NiCoCrAIY/BaF2/CaF2/WSe2/Y Solid Lubrican

BaF2/CaF2 is well-known for the solid lubricant properties at evaluated temperature and used as self-lubricants in vacuum and ambient air.

会议

Solid-lubricantHightemperatureFictionWearFluorides

LiBH4 Confined in Nitrogen-Doped Ordered Mesoporous Carbons for Hydrogen Storage

Nitrogen-doped ordered mesoporous carbon has been synthesized and used to confine LiBH4 to improve its dehydrogenation properties.The carbon has a high BET specific surface up t0 448.25m2/g with pore

会议

LiBH4Hydrogen storageN-doped mesoporous carbonsConfinement

Modulated Synthesis of UiO-67 for High Resistance to CH2Cl2

UiO-67 has been synthesizedby using the acetic acid as a template via conventional electric(CE)heating method.With the same adding of acetic acid.differentcrystallinity and pore structure are obtained

会议

Metal-organic frameworkUiO-67Modulated synthesis

PtCo Nanoparticles Supported on Carbon for Hydrolysis of Ammonia Borane

Ammonia borane received extensive attention due to its hydrogen content as high as 19.6%.In present article we prepared the Pt-Co/C catalyst via ultrasonic immersion method and in situ reduction metho

会议

PtCo nanoparticlesCatalytic hydrolysisPorous carbonAmmonia borane

掺杂纳米硅的制备与电输运特性研究

采用甚高频等离子体增强化学气相沉积(VHF-PECVD)系统制备了一系列不同硼掺杂浓度的氢化非晶硅薄膜。然后对原始样品进行800℃退火处理，使薄膜由非晶结构向晶化结构转变，得到含有纳米晶粒的掺杂纳米硅薄膜。

会议

纳米硅硼掺杂激活能

掺镍纤维的水泥基复合材料的电磁屏蔽性能

电磁波技术的广泛应用导致电磁干扰与污染日益严重，采取电磁屏蔽措施能够有效地防范这些危害。实验采用不同的方法分散镍纤维屏蔽介质，然后掺入到水泥材料中制得水泥基复合屏蔽材料，研究了屏蔽介质的分散方式、掺量、试样厚度对屏蔽性能的影响：利用四探针测试仪、电子探针等手段表征了复合材料的电导率和屏蔽介质的分散均匀性。

会议

电磁屏蔽材料水泥基复合材料镍纤维

Preparation and Characterization of a Magnetic Binary System Comprise of γ-Fe2O3and α-FeO(OH)Nanopar

与本文相关的学术论文