【摘 要】
：
The microstructure and mechanical properties of an HB400 grade abrasion resistant steel was studied with an emphasis on the initial microstructure before intercritical heat treatment.The result shows
【机 构】
：
Institute of Research of Iron and Steel(IRIS)of Sha-steel,Zhangjiagang,Jiangsu,215625,China
论文部分内容阅读
The microstructure and mechanical properties of an HB400 grade abrasion resistant steel was studied with an emphasis on the initial microstructure before intercritical heat treatment.The result shows that the initial microstructure,before intercritical quenching(Q),has a great effect on the final microstructure and mechanical properties.The hardness of samples with two initial microstructures,i.e.bainite and martensite,is almost the same,but the toughness and wear resistance of the latter are much higher than that of the former,after intercritical quenching plus tempering(Q+T)process.The one with bainite as the initial microstructure has a final microstructure of block-type tempered martensite and ferrite with martensite islands inside.Cracks may easily occur at the boundaries of martensite islands and pass through the low angle grain boundaries in the ferrite.By contrast,the one with martensite as the initial microstructure has a uniformly distributed tempered martensite and needle-like ferrite.The boundaries between them are high angle grain boundaries,and hence cracks may be arrested or deflected,resulting in a higher toughness.
其他文献
Multi-pass deformation simulation tests were performed on V-N microalloyed steels with different nitrogen addition by using a Gleeble-3800 thermo-mechanical simulator and the corresponding continuous
Instead of off-line quenching and tempering(QT),on-line ausforming(non-recrystallization controlled roling)and direct quenching(DQ)was employed to improve the toughness of low alloy steel with yield s
A cost effective alloy design based on niobium microalloying was developed by Shagang for the production of 32 mm gage K60-E2 steel plate for manufacturing LSAW pipes of 1422 mm diameter.Two metallurg
The effect of Mo addition on the precipitation of carbides both in austenite and ferrite of Nbbearing HSLA steel were investigated by stress relaxation and transmission electron microscopy(TEM).Experi
International Standard ISO 6892-2 maintains that strain rate variations can induce the measurement uncertainty of mechanical properties in tensile testing,which will imperil the reliability of tension
The microstructure,mechanical property and precipitation behavior in a low carbon Nb-Ti micro-alloyed steel were investigated using dilatometer,optical microscopy and transmission electron microscope.
The influence of Nb,Mo,Cr and B on phase transformations and mechanical properties are studied in a 0.15C-2.0Mn-0.3Si-0.020Ti dual phase steel separately and in combination.The formation and decomposi
Deformation processes of microalloyed steels,both during hot and cold processing,are characterized by complex interactions between fine strain-induced precipitates and deformation activated movement o
The use of niobium as a microalloying element in high strength steels is now well-known and widely adopted.However,with recent advances in thermo-mechanical processing,inclusive of ultrafast cooling t
We examined the effects of micro-texture and grain shape on the delamination of hot-rolled high strength low alloyed(HSLA)steel sheets through a series of uniaxial tensile tests.Prior to testing,the H